** DIN X3CrNiMoBN17-13-3/W-Nr1.4910 - DATA SHEET **High temperature high strengthsteel and superalloyPRODUCT DESCRIPTI...
** DIN X3CrNiMoBN17-13-3 / W-Nr 1.4910 - DATA SHEET **
High temperature high strength steel and superalloy
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
MATERIAL SPECIFICATIONS
※ DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999)
AVAILABLE SHAPES
Black bar /Flat bar /square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
CHEMICAL COMPOSITION (WEIGHT %)
C(％): ≤0.04
Si(％): ≤0.75
Mn(％): ≤0.20
P(％)≤: 0.035
S(％)≤: 0.015
Cr(％): 16.0～18.0
Ni(％): 12.0～14.0
Mo(％): 2.00～2.80
Other(％): B 0.0015～0.0050, N 0.10～0.18
Si(％): ≤0.75
Mn(％): ≤0.20
P(％)≤: 0.035
S(％)≤: 0.015
Cr(％): 16.0～18.0
Ni(％): 12.0～14.0
Mo(％): 2.00～2.80
Other(％): B 0.0015～0.0050, N 0.10～0.18
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃: 1150～750
Heat treatment temperature /℃ | annealing: -
Heat treatment temperature /℃ | quenching or solution: 1020 ~ 1100 air / water
Heat treatment temperature /℃ | tempering: -
Heat treatment temperature /℃ | ageing: -
Condition: solution treatment
Mechanical property under room temperature |σb/MPa: 550~750
Mechanical property under room temperature |σs≥/MPa: 260
Mechanical property under room temperature |δ5≥(％): 35
Mechanical property under room temperature |Akv(DVM): -
Heat stability temperature/℃: -
Non-scale temperature in air /℃: -
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200: 170
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 148
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 134
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 140
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 127
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 121
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300: 148
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400: 134
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500: 140
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600: 127
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700: 121
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800: -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600: 205
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700: 84
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800: 33
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 141
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700: 52
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: 20
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800: 20
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
These materials must stand up to high heat, extreme oxidation potential and recycling.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 3000mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.