※DINX20CrMoV12-1 /W-Nr1.4922 - DATA SHEET ※High temperature high strengthsteel and superalloyPRODUCT DESCRIPTIONThe ...

※ DIN X20CrMoV12-1 / W-Nr 1.4922 - DATA SHEET ※

High temperature high strength steel and superalloy

PRODUCT DESCRIPTION

The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) if necessary for special purpose.

Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.

Bars are usually supplied bright in the solution annealing condition.

Final heat treatment - heat treatment / QT / solution treatment

MATERIAL SPECIFICATIONS

※ DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999)

AVAILABLE SHAPES

Black bar /Flat bar /square bar

Bright - peeled + polishing /centerless grinding /peeled + slidabrading

Forged - ring /pipe casing /discs /shaft

CHEMICAL COMPOSITION (WEIGHT %) - DIN X20CrMoV12-1

C(％):     0.17～0.23
Si(％):    ≤0.50
Mn(％):  ≤1.00
P(％)≤:   0.030
S(％)≤:   0.030
Cr(％):    10.0～12.5
Ni(％):    0.30～0.80
Mo(％):   0.80～1.20
Other(％): V 0.25～0.35

MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS

Hot forming temperature /℃: 1100～850

Heat treatment temperature /℃ | annealing: 750~780

Heat treatment temperature /℃ | quenching or solution: 1030 ~ 1070 air / oil

Heat treatment temperature /℃ | tempering: 720~770

Heat treatment temperature /℃ | ageing: -

Condition: heat treatment

Mechanical property under room temperature |σb/MPa: 700~ 850

Mechanical property under room temperature |σs≥/MPa: 500

Mechanical property under room temperature |δ5≥(％): 16

Mechanical property under room temperature |Akv(DVM): 41

Heat stability temperature/℃: 580

Non-scale temperature in air /℃: 700

MECHANICAL PROPERTY UNDER HIGH TEMPERATURE

Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|200:    430
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|300:    392
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|400:    350
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|500:    280
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|600:    160
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|700:   -
Mechanical property above 200℃ σ0.2/MPa，at following temperature /℃|800:    -

Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|600:   127
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|700:    -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|800:    -
Creep rupture strength /MPa，at following time/h and temperature /℃|1000h|900:    -

Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|600:   103
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|700:   -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|800:    -
Creep rupture strength /MPa，at following time/h and temperature /℃|10000h|900:    -

Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|600: 59

Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|700:   -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|800:    -
Creep rupture strength /MPa，at following time/h and temperature /℃|100000h|900:    -

TYPICAL APPLICATIONS

Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.

Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor

Turbine engine parts - mechanical gears, gear shaft, main axis, blade

Mechanical parts - bolt and nut, fastener

Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.

INVENTORY - forged bar
Diameter: 120mm
Quantity: 1150kg

TECHNICAL SALES ASSISTANCE

If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers.

Product engineer: Mr. Chen, Mr.Jiang
Tel: 86-816-3307163, 365 3300

Email: sales@ccsteels.com

PRODUCT PROFILE

Round bar / Wire rod (Diameter): 0.50mm to 3000mm

Square bar / Flat bar: 3mm to 2000mm

Plate / Sheet steel / Steel strip: 0.1mm to 2500mm

Width: 8mm to 2500mm

Length: random length or based on the customer's special requirement.

Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.

Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.

Hot search：DIN X20CrMoV12-1

Previous page：W-Nr 1.4921
Last page：W-Nr 1.4922

Share to：

DIN X20CrMoV12-1
2014-09-12 09:54:16 Origin： Remark：0 Click：

Total list

Monthly rank

DIN X20CrMoV12-1 2014-09-12 09:54:16 Origin： Remark：0 Click：

Extend reading：

Total list

Monthly rank

DIN X20CrMoV12-1
2014-09-12 09:54:16 Origin： Remark：0 Click：