X8CrMnN18-18 Forgings, Ring, Bar
2019-12-10 11:14:53 Origin: Remark:0 Click:
Non-magnetic X8CrMnN18-18 Forge Bar & Plate machined, X8CrMnN18-18 forging ring - Technical standards - DIN SEW 390 (1991) or by agreement.
TECHNICAL DATA SHEET - X8CrMnN18-18
MATERIAL CATEGORY: Non-magnetic stainless steel and alloy
AVAILABLE STOCK: Round bar Dia. 50 ~ 210mm, ESR ingot
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: DIN SEW 390 (1991)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.12
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): 17.5 ~ 20.0
Phosphorus, P (%) ≤: 0.060
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 17.5 ~ 20.0
Nickel, Ni (%): ≤ 1.00
Molybdenum, Mo (%): -
Nitrogen, N (%): 0.40 ~ 0.70
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 950℃
Quenching or solution treatment temperature: 1020 ~ 1120℃
Tensile strength, Rm ≥ MPa: 750 ~ 950
Yield strength, σ0.2 ≥ MPa: 480
Elongation, A5 ≥ (%): 40.0
Impact, Akv ≥/J: 200 (transversal value)
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
The alloy is usually produced by EAF / AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered.
PROFILE & DIMENSIONS & SERVICE
Round bar & Disc (diameter): 50mm to 850mm
Square bar / Flat bar: 6mm to 600mm
Heavy / middle plate via hot rolled: T10 ~ 400mm X W20 ~ 1000mm X Lmm
Forging piece: stepped shafts, other different shapes based on OEM.
Round bar & Disc (diameter): 50mm to 850mm
Square bar / Flat bar: 6mm to 600mm
Heavy / middle plate via hot rolled: T10 ~ 400mm X W20 ~ 1000mm X Lmm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production teams, E-mail: sales@ccsteels.com
Hot search:X8CrMnN18-18 forgings round bar ring
Previous page:K41650
Last page:ASTM A565 Grade 616
Total list
Monthly rank
- 6Z50MC18-4 Forgings, Bars
- 4AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4M-152 / S64152 / 1.4938 Forgings
- 4AISI 422 Flat bar / S42200 Forgings
- 417-4PH Flat bar
- 3S17400 Forged Valve Body
- 3ASTM A565 grade 616
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3S13800 bar, S13800 plate
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel