Specifications S16800 Ex-stock, S16800 Suppliers, Properties S16800 Forging Bar Plate, S16800 Technical Specifications Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL TECHNICAL DATA SHEET - S16800
CATEGORY - 15Cr-8Ni-2Mo Austenitic steel
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
The alloy is usually produced by AOD followed by electroslag refining (ESR).
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - solution treatment.
ASTM A959 (2004), A276
Black, Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft, flat bar
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.05 ~ 0.10
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.5 ~ 16.5
Ni (％): 7.50 ~ 9.50
Mo (％): 1.50 ~ 2.00
N (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥MPa: 622
Yield strength, σ0.2/≥MPa: 275
Elongation, δ (％)≥: 40
Reduction of area, ф (％)≥: -
Hardness ≤(HBW): 241
Hardness | ≤HRB: 100
Cold bending property: N
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to email (firstname.lastname@example.org) or call our resident team of qualified production engineers
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1200mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.