DIN X20CrMoWV12-1 datasheet,DIN X20CrMoWV12-1 chemical,DIN X20CrMoWV12-1 heat treatment
Home > Superalloy > Text

DIN X20CrMoWV12-1
2014-09-13 09:05:27   Origin:   Remark:0 Click:

※DINX20CrMoWV12-1 /W-Nr1.4935- DATA SHEET ※MATERIAL CATEGORY: High temperature high strengthsteel and superalloyPRODU...
※ DIN X20CrMoWV12-1 / W-Nr 1.4935 - DATA SHEET ※ 
 
MATERIAL CATEGORY
High temperature high strength steel and superalloy 
 
PRODUCT DESCRIPTION
The alloy is usually produced by AOD/VIM/VOD followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the solution annealing condition.
Final heat treatment - heat treatment / QT / solution treatment
 
MATERIAL SPECIFICATIONS 
 DIN 17742, 17460, 17480  (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999)
 
AVAILABLE SHAPES  
Black bar /Flat bar /square bar  
Bright - peeled + polishing /centerless grinding /peeled + slidabrading
Forged - ring /pipe casing /discs /shaft
 
CHEMICAL COMPOSITION (WEIGHT %)  -  W-Nr.1.4935 
C(%):     0.17~0.25
Si(%):    0.10~0.50
Mn(%):   0.30~0.80
P(%)≤:   0.045
S(%)≤:   0.030
Cr(%):    11.0~12.5
Ni(%):    0.30~0.80
Mo(%):   0.80~1.20
Other(%):    W 0.40~0.60,V0.25~0.35
 
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot forming temperature /℃:    1150~900
Heat treatment temperature /℃ | annealing:   770~800    
Heat treatment temperature /℃ | quenching or solution:  1000 ~ 1070 air / oil 
Heat treatment temperature /℃ | tempering: 690~780
Heat treatment temperature /℃ | ageing:   630~750
Condition: heat treatment
Mechanical property under room temperature |σb/MPa: 780~ 930                  
Mechanical property under room temperature  |σs≥/MPa:  590    
Mechanical property under room temperature |δ5≥(%):   14      
Mechanical property under room temperature |Akv(DVM):  34       
Heat stability temperature/℃:   580
Non-scale temperature in air /℃:   600
          
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|200:    539              
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|300:    490           
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|400:    441           
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|500:    373            
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|600:    137         
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|700:   -
Mechanical property above 200℃ σ0.2/MPa,at following temperature /℃|800:    -
 
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|600:   157
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|700:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|1000h|900:    -

Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|600:   108
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|700:   -
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|10000h|900:    -

Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|600:  59
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|700:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|800:    -
Creep rupture strength /MPa,at following time/h and temperature /℃|100000h|900:    -
 
TYPICAL APPLICATIONS 
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Gas turbine
Turbine blade
Fuel nozzle
Heat treating fixture
Furnace muffle
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
 
INVENTORY - Forged bar
Diameter: 115mm, 130mm
Quantity:  1120kg
 
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers.
Product engineer: Mr. Chen, Mr.Jiang
Tel: 86-816-3307163, 365 3300
 
PRODUCT PROFILE  
Round bar / Wire rod (Diameter):  0.50mm to 3000mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.

     