Aircraft steel D6AC
2016-01-22 10:25:10   Origin:   Remark:0 Click:

Specifications D6AC Datasheet, Inventory D6AC Chemical, Suppliers D6AC Property Steelmaking, D6AC ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working, Peeled or rough turned machining. Technical specification - ASTM A29/29M. We also possess the advanced precision machining equipments for catering for your different special requirements.
TECHNICAL SPECIFICATIONS Aircraft steel D6AC

MATERIAL CATEGORY: Ultra high strength 1520Mpa Asteel
MAIN FEATURES: D6AC VAC-ARC steel is a medium carbon, low alloy, ultra high strength 1471Mpa steel primarily designed for high strength structural applications
D6AC steel is produced by the consumable electrode vacuum arc remelting process to provide optimum cleanliness and preferred ingot structure, which in turn provide optimum transverse mechanical properties.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS BV
CHEMICAL COMPOSITION (WEIGHT %)
C (%):    0.42 ~ 0.48
Si (%):    0.15 ~ 0.35
Mn (%):  0.60 ~ 0.90

P (%)≤:  0.015
S (%)≤:  0.015
Cr (%):   0.90 ~ 1.20
Ni (%):    0.40 ~ 0.70
Mo (%):  0.90 ~ 1.10
V (%):     0.05 ~ 0.10
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Heat treatment - Austenitized at 900℃ . Oil quenched and air cooled, or salt quenched at 205 ~ 220 ℃ for 10 minutes and air cooled
Tensile strength σb≥/MPa:  1520.0
Yield strength σs≥/MPa:      1422.0
Elongation δ5≥(%):            9
AKV≥/J:                             -
Hardness HRC:                   45
Working pressure /MPa:     932.0
Bursting pressure /MPa:     1275.0
MELTING PROCESS
VIM + ESR Melted
TYPICAL APPLICATIONS
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rod
Multidiameter shaft
Pressure vessel
  