STS631 Aged RH950
2020-02-27 15:54:58 Origin： Remark：0 Click：
STS631 RH950 Steel Ex-stock, STS631 RH950 Suppliers & Manufacturers, STS631 RH950 Forging Bar Plate machined, STS631 RH950 Exporters Technical specifications - KS D3706 - 2001 / 2006. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL DATA SHEET - KS D3706 Grade STS631
TECHNICAL SPECIFICATIONS: KS D3706 - 2001/2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.09
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 6.50 ~ 7.75
Mo (%): -
Al (%): 0.75 ~ 1.50
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1000 ~ 1100 Deg.C
Tensile strength, σb/ ≥ MPa:1030
Yield strength, σ0.2/ ≥ MPa: 880
Elongation, δ (％) ≥: 20.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): -
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1000 ~ 1100 Deg.C
Tensile strength, σb/ ≥ MPa:1030
Yield strength, σ0.2/ ≥ MPa: 880
Elongation, δ (％) ≥: 20.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): -
Aged RH950, 955 Deg.C, air cooled
Tensile strength, σb/ ≥ MPa:1230
Yield strength, σ0.2/ ≥ MPa: 1030
Elongation, δ (％) ≥: 4.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): -.
Tensile strength, σb/ ≥ MPa:1230
Yield strength, σ0.2/ ≥ MPa: 1030
Elongation, δ (％) ≥: 4.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): -.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：STS631 RH950
Last page：STR 31
Total list
Monthly rank
- 6Z50MC18-4 Forgings, Bars
- 4AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4M-152 / S64152 / 1.4938 Forgings
- 4AISI 422 Flat bar / S42200 Forgings
- 417-4PH Flat bar
- 3S17400 Forged Valve Body
- 3ASTM A565 grade 616
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3S13800 bar, S13800 plate
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel