2Cr12MoV Forgings, Round bar, Shaft
2024-06-11 12:48:12 Origin： Remark：0 Click：
Turbine Blade Steel 2Cr12MoV Martensitic type Mechanical Parts at high tmperature Stock Available Round bar, Flat bar and bolts and nuts
TECHNICAL SPECIFICATION - Blade Steel 2Cr12MoV
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Stock Available: Round bar diam. 20 ~ 180mm
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Stock Available: Round bar diam. 20 ~ 180mm
MATERIAL SPECIFICATIONS - GB/T 20410 - 2006
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.18 ~ 0.24
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.30 ~ 0.80
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Nickel, Ni (%): 0.30 ~ 0.60
Chromium, Cr (％): 11.00 ~ 12.50
Molybdenum, Mo (％): 0.80 ~ 1.20
Copper, Cu (％): ≤ 0.25
Vanadium, V (%): 0.25 ~ 0.35
Titanium, Ti (%): -
Boron, B (%): -
Niobium, Nb (%): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hardness after annealing ≤HBS: 255 Max.
Tensile strength, Rm ≥ MPa: 900 ~ 1050
Yield strength, Rp0.2 ≥ MPa: 700
Elongation, A5 ≥ (%): 13.0
Reduction of area, Z ≥ (%): 35.0
Impact strength, AKu ≥ J: 20
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
If you meet further on any technical enquiry, pleased to email (sales@ccsteels.com) or call our resident team of qualified production engineers.
Hot search：
Total list
Monthly rank
- 6Z50MC18-4 Forgings, Bars
- 4AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4M-152 / S64152 / 1.4938 Forgings
- 4AISI 422 Flat bar / S42200 Forgings
- 417-4PH Flat bar
- 3S17400 Forged Valve Body
- 3ASTM A565 grade 616
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3S13800 bar, S13800 plate
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel