1.4938 / X12CrNiMoV12 / S64152 / M-152
2024-09-23 08:46:03 Origin: Remark:0 Click:
Martensitic high tensile stainless steel, M-152 Stock Available 1.4938 Round bar, flat bar, Forging piece, Heat treatment
TURBINE BLADE STEEL - 1.4938 & X12CrNiMoV12-3 & S64152 & M-152
INVENTORY & STOCKLIST - Round bar diam.40mm ~ 210mm, ESR ingot
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Customizing special material is welcome.
HS Code For Customs - 72221100 / 72222000 / 72223000
TYPICAL CHEMICAL COMPOSITIONS (mass fraction %)
Carbon, C (%): 0.08 ~ 0.13
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): 0.50 ~ 0.90
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.0 ~ 12.5
Nickel, Ni (%): 2.00 ~ 3.00
Molybdenum, Mo (%): 1.50 ~ 2.00
Manganese, Mn (%): 0.50 ~ 0.90
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 11.0 ~ 12.5
Nickel, Ni (%): 2.00 ~ 3.00
Molybdenum, Mo (%): 1.50 ~ 2.00
Nitrogen, N (%): 0.01 ~ 0.05
Vanadium, V (%): 0.25 ~ 0.40
Copper, Cu (%): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition / Bar, forings: quenched and tempered, + SRA
Tensile strength, Rm ≥ MPa: 930 ~ 1130
Yield strength, Rp0.2 ≥ MPa: 780
Elongation, A5 ≥ (%): 14.0
Elongation, A5 ≥ (%): 14.0
Reduction of area, Z ≥ (%): -
Hardness | HB: 280 ~ 352
PRODUCT PROFILE & SERVICE
Round bar & disc & Rod (diameter): 5.5mm to 650mm
Square bar / flat bar: 10mm to 700mm
Heavy/middle plate via hot rolled: T50 - 400mm X W80- 1000mm X L1000 ~ 4000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
Square bar / flat bar: 10mm to 700mm
Heavy/middle plate via hot rolled: T50 - 400mm X W80- 1000mm X L1000 ~ 4000mm
Forging piece: stepped shafts, and other different shapes based on OEM.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Hot search:
Previous page:1.4923 ESR / X22CrMoV12
Last page:最后一页