TECHNICAL DATA SHEET - DIN 15CrNi6 & W-Nr 1.5919
MATERIAL CATEGORY: Carburizing structural steel
PRODUCT DESCRIPTION
Thermal expansion coefficients compatible with low alloy steel turbine casing materials.
Lower design and operating risks
Simplified design for bolting configuration compared with martensitic steels or high nickel alloys.
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - heat treatment / QT 
MATERIAL SPECIFICATIONS - DIN EN 10084 (1998), DIN 17210 (1986)
CHEMICAL COMPOSITION (mass weight - %)      
Carbon, C (%): 0.14 ~ 0.19
Silicon, Si (%): ≤ 0.40
Manganese, Mn (%): 0.40 ~ 0.60
Phosphorus, P (%) ≤:  0.035
Sulfur, S (%) ≤: 0.035
Chromium, Cr (%): 1.40 ~ 1.70
Molybdenum, Mo (%): -
Nickel, Ni (%): 1.40 ~ 1.70
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃:    1150~850
Heat treatment temperature /℃| annealing:    650~700
Heat treatment temperature /℃|carburization: 900~950
Heat treatment temperature /℃|quenchingⅠ(center):    840~870
Heat treatment temperature /℃|quenchingⅡ(surface):   800~830, Oil
Heat treatment temperature /℃|tempering:    170~210
HBS≤:  217
|size /mm:   φ11
Tensile strength, |σb/MPa:    960~1270
Yield strength, |σs≥/MPa:  685
Elongation, |δ5(%)≥: 8.0
Reduction of area, |ψ(%)≥: 35.0
Impact strength, |AKV/J: 41
|size /mm:   φ30
|σb/MPa:    880~1180
|σs≥/MPa:  635
|δ5(%)≥:    8
|ψ(%)≥:     40
|AKV/J:       41
|σb/MPa:    780~1080
|σs≥/MPa:  540
|δ5(%)≥:    10
|ψ(%)≥:      40
|AKV/J:       -       
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
 TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners,
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut, Multidiameter shaft, Pressure vessel.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers.- Email: 
sales@ccsteels.com.

Hot search:15CrNi6

Previous page:1.5918
Last page:1.5919

Share to: