1.5023
2020-02-18 13:10:20 Origin： Remark：0 Click：
Spring steel 1.5023 Round bar, flat bar, plate Steelmaking, ESR melted, Blooming, Hot forging rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold machined. Specification - DIN 17221.
Official Test Certificate: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - Grade W-Nr.1.5023
MATERIAL TYPE: Spring Steel
MATERIAL STANDARDS: DIN 17221
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.35 ~ 0.42
Si (％): 1.50 ~ 1.80
Mn (％): 0.50 ~ 0.80
P (％)≤: 0.025
S (％)≤: 0.025
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): -
Mo (%): -
V (%): -
Other(％): Cu + 10Sn -/+ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Range of size/mm|flat bar: 10
Range of size/mm|round bar: 12
Mechanical property ≥|σb/MPa: 1180～1370
Mechanical property ≥|σs/MPa: 1030
Mechanical property ≥|δ5(%): 6.0
Mechanical property ≥|ψ(%): -
Mechanical property ≥|Akv /J: -
Range of size/mm|round bar: 12
Mechanical property ≥|σb/MPa: 1180～1370
Mechanical property ≥|σs/MPa: 1030
Mechanical property ≥|δ5(%): 6.0
Mechanical property ≥|ψ(%): -
Mechanical property ≥|Akv /J: -
HOT WORKING & HEAT TREATMENT
Hot working temperature /℃: 1100~850
Thermal forming temperature /℃: 900~820
Heat treatment temperature/℃|annealing /℃: 640～680
Heat treatment temperature/℃|normalizing /℃: 830~860
Heat treatment temperature/℃|quenching /℃: 830～860 Water
Heat treatment temperature/℃|tempering /℃: 430～500
Hardness after annealing ≤HBW: 217
Thermal forming temperature /℃: 900~820
Heat treatment temperature/℃|annealing /℃: 640～680
Heat treatment temperature/℃|normalizing /℃: 830~860
Heat treatment temperature/℃|quenching /℃: 830～860 Water
Heat treatment temperature/℃|tempering /℃: 430～500
Hardness after annealing ≤HBW: 217
MAIN FEATURES & PERFORMANCE REQUIREMENTS
Spring steel is specialized in producing the spring and elastic components due to its elasticity under the condition of quenching and tempering. The elasticity of steel depends on its capacity of elastic deformation.
This allows objects made of spring steel to return to their original shape despite significant bending or twisting occurs.
Spriing steel should possess excellent combination property, such as mechanical property (limit of elasticity, ultimate strength, yield ratio), relaxation resistant, fatigue property, hardenability, physical and chemical property (heat resistance,low temperature resistant, antioxidation, corrosion resistance). To meet the above performance requirement, Spring steel has fine metallurgical quality ( high purity, homogeneity), excellent surface quality ( specially on surface defect and decarburization), precise external form and dimensions.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：1.5023
Previous page：STS630 H1025
Last page：SAE 2340