1.5223
2020-03-26 16:58:58 Origin： Remark：0 Click：
Specifications 1.5223, Alloy 1.5223 Suppliers, Properties 1.5223 Forging Bar Plate, ESR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - W-Nr 1.5223
MATERIAL CATEGORY: hardened and tempered steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF / VD / LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.38 ~ 0.45
Silicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 1.60 ~ 1.90
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
Vanadium, V (％): 0.07 ~ 0.12
Silicon, Si (％): 0.15 ~ 0.35
Manganese, Mn (％): 1.60 ~ 1.90
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): -
Molybdenum, Mo (％): -
Nickel, Ni (％): -
Vanadium, V (％): 0.07 ~ 0.12
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃| annealing: 640～680
Heat treatment temperature /℃| Normalizing: 860～890
Heat treatment temperature /℃| Quenching: 840～870 Water
Heat treatment temperature /℃| Tempering: 480～650
Hardness after annealing ≤HBS: 217
Heat treatment temperature /℃| annealing: 640～680
Heat treatment temperature /℃| Normalizing: 860～890
Heat treatment temperature /℃| Quenching: 840～870 Water
Heat treatment temperature /℃| Tempering: 480～650
Hardness after annealing ≤HBS: 217
Steel dimension /mm: ≤16
Tensile strength, σb ≥ MPa: 980 ~ 1270
Yield strength, σs≥ /MPa: 885
Elongation, δ 5 ≥ (%): 10
Reduction of area, ψ ≥ (%): 30
Impact strength, AKV ≥ J: 21
Tensile strength, σb ≥ MPa: 980 ~ 1270
Yield strength, σs≥ /MPa: 885
Elongation, δ 5 ≥ (%): 10
Reduction of area, ψ ≥ (%): 30
Impact strength, AKV ≥ J: 21
Steel dimension /mm: 17 - 40
|σb≥/MPa: 980 ~ 1180
|σs≥/MPa: 785
|δ5≥/(%): 11
|σb≥/MPa: 980 ~ 1180
|σs≥/MPa: 785
|δ5≥/(%): 11
|ψ≥/(%): 35
|AKV≥/J: 27
|AKV≥/J: 27
Steel dimension /mm: 41 - 100
|σb≥/MPa: 880 ~ 1030
|σs≥/MPa: 685
|δ5≥/(%): 12
|ψ≥/(%): 40
|AKV≥/J: 34
|σb≥/MPa: 880 ~ 1030
|σs≥/MPa: 685
|δ5≥/(%): 12
|ψ≥/(%): 40
|AKV≥/J: 34
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nut.
Multidiameter shaft, Pressure vessel.
PRODUCT PROFILE
Round bar (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 450mm
Plate / Sheet steel / Steel strip: 0.1mm to 500mm
Width: 8mm to 50000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shaft, other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200 mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
Hot search：1.5223
Previous page：1.5141
Last page：A182 Gr. S41000
Total list
Monthly rank
- 7224CrMo5
- 4438NCD4
- 3926NiCrMoV14-5
- 31ASTM A739 Gr. B11
- 28EN52 & EN 52
- 27XC38
- 26EN 14B
- 25815M17
- 24EN 38
- 2327NiCrMoV11-6