X21CrMoV12-1
2024-03-19 17:05:49 Origin： Remark：0 Click：
Quenched & Tempered Alloy Steel X21CrMoV12-1, The alloy is used for larger preshaped components in turbine and generator installations, shafts and discs.
TECHNICAL DATASHEET - Grade X21CrMoV12-1
Material Category: Hardened and tempered steel
Material Specification - SEW 555 or by agreement
Melting process way - EF + ESR
HS code for Customs: 7228 4000 / 7228 5000 / 7228 6000
Main Chemical composition (mass weight - %)
Carbon, C (％): 0.20 ~ 0.26
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.30 ~ 0.80
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.00 ~ 12.50
Molybdenum, Mo (％): 0.80 ~ 1.20
Nickel, Ni (％): 0.30 ~ 0.80
Vanadium, V (％): 0.25 ~ 0.35
Ferrum, Fe (％): remainder.
Material Category: Hardened and tempered steel
Material Specification - SEW 555 or by agreement
Melting process way - EF + ESR
HS code for Customs: 7228 4000 / 7228 5000 / 7228 6000
Main Chemical composition (mass weight - %)
Carbon, C (％): 0.20 ~ 0.26
Silicon, Si (％): ≤ 0.35
Manganese, Mn (％): 0.30 ~ 0.80
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.00 ~ 12.50
Molybdenum, Mo (％): 0.80 ~ 1.20
Nickel, Ni (％): 0.30 ~ 0.80
Vanadium, V (％): 0.25 ~ 0.35
Ferrum, Fe (％): remainder.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 269
Tensile strength, |σb≥/MPa: 750 ~ 900
Yield strength, |σs≥/MPa: 600
Elongation, |δ5≥/(%): 11.0
Reduction of area, |ψ≥/(%): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / VD / LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 6mm to 650mm
Plate / Steel strip: 1.0mm to 200mm
Steel sheet: thickness 1.0 ~ 4.0mm, width 10 ~ 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
Forged steel shape: stepped shafts, other different shapes based on OEM
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 269
Tensile strength, |σb≥/MPa: 750 ~ 900
Yield strength, |σs≥/MPa: 600
Elongation, |δ5≥/(%): 11.0
Reduction of area, |ψ≥/(%): 40.0
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / VD / LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 6mm to 650mm
Plate / Steel strip: 1.0mm to 200mm
Steel sheet: thickness 1.0 ~ 4.0mm, width 10 ~ 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
Forged steel shape: stepped shafts, other different shapes based on OEM
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：X21CrMoV12-1
Previous page：1.6945
Last page：20Cr1Mo1VTiB
Total list
Monthly rank
- 6124CrMo5
- 5542Cr4Mo2
- 52EN 14B
- 4838NCD4
- 47EN 38
- 4534CrNiMo4
- 44ASTM A739 Gr. B11
- 43EN 355
- 42X20CrMoV12-1
- 4240Cr4