JIS G4108 Technical specifications of Bolting materials for high temperature service SNB23-3 Round bar, Flat bar, Heat treatment
MATERIAL DATA SHEET - JIS SNB23-3
MATERIAL CATEGORY: Alloy steel bolting materials for high temperature service
MATERIAL SPECIFICATIONS: JIS G4108 -2007
MATERIAL SPECIFICATIONS: JIS G4108 -2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.37 ~ 0.44
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.37 ~ 0.44
Silicon, Si (%): 0.20 ~ 0.35
Manganese, Mn (%): 0.60 ~ 0.95
Manganese, Mn (%): 0.60 ~ 0.95
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): 0.65 ~ 0.95
Nickel, Ni (%): 1.55 ~ 2.00
Molybdenum, Mo (%): 0.20 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Diam.: 75mm Max.
Tensile strength, Rm ≥ MPa: 1000
Yield strength, Rp0.2 ≥ MPa: 890
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
Hardness | HBW ≤: 293 ~ 363
Yield strength, Rp0.2 ≥ MPa: 890
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
Hardness | HBW ≤: 293 ~ 363
Diam.: 75mm ~ 150mm
Tensile strength, Rm ≥ MPa: 1000
Yield strength, Rp0.2 ≥ MPa: 890
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
Hardness | HBW ≤: 302 ~ 375
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
Hardness | HBW ≤: 302 ~ 375
MELTING PROCESS AND FEATURES
The steels shall be manufactured by melting process EF + ESR, EAF+ LF + VD, ESR Melted or by agreement.
Spring steel should possess excellent combination property, such as mechanical property (limit of elasticity, ultimate strength, yield ratio), relaxation resistant, fatigue property, hardenability, physical and chemical property (heat resistance,low temperature resistant, antioxidation, corrosion resistance). To meet the above performance requirement, Spring steel has fine metallurgical quality ( high purity, homogeneity), excellent surface quality ( specially on surface defect and decarbur-ization), precise external form and dimensions.
PRODUCT PROFILE & DIMENSION
Round bar & Disc (diameter): 5.50mm to 650mm
Square bar / Flat bar (width X thickness): 10mm to 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Steel sheet / plate: T0.50 ~ 50mm X W10 ~ 2000mm X random length or in coil form.
The steels shall be manufactured by melting process EF + ESR, EAF+ LF + VD, ESR Melted or by agreement.
Spring steel should possess excellent combination property, such as mechanical property (limit of elasticity, ultimate strength, yield ratio), relaxation resistant, fatigue property, hardenability, physical and chemical property (heat resistance,low temperature resistant, antioxidation, corrosion resistance). To meet the above performance requirement, Spring steel has fine metallurgical quality ( high purity, homogeneity), excellent surface quality ( specially on surface defect and decarbur-ization), precise external form and dimensions.
PRODUCT PROFILE & DIMENSION
Round bar & Disc (diameter): 5.50mm to 650mm
Square bar / Flat bar (width X thickness): 10mm to 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Steel sheet / plate: T0.50 ~ 50mm X W10 ~ 2000mm X random length or in coil form.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com.) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com.) our resident team of qualified production engineers.
Hot search:
Previous page:27NiCrMoV16-7
Last page:1.6963
Total list
Monthly rank
- 3624CrMo5
- 3338NCD4
- 33EN 14B
- 3342Cr4Mo2
- 28EN33 / EN 33
- 27ASTM A739 type B11
- 22EN 38
- 22XC38
- 2231Ni10Cr3Mo6
- 2226NiCrMoV11-5