Specification GB/T 20410 Steels 1Cr11MoNiW1VNbN Turbine Mechanical Parts, Stock Available Round bar 1Cr11MoNiW1VNbN Flat bar, Bolts, Nuts
MATERIAL DATASHEET - GB 1Cr11MoNiW1VNbN
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Working Temperature: 600 ℃ Max.
MATERIAL CATEGORY - Steels for Turbine bolts and nuts at high tmperature
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
Working Temperature: 600 ℃ Max.
Stock Available: Round bar diam. 50 ~ 180mm
MATERIAL SPECIFICATIONS - GB/T 20410 - 2006
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.12 ~ 0.16
Silicon, Si (%): 0.30
Manganese, Mn (%): 0.30 ~ 0.70
Phosphorus, P (%) ≤: 0.020
Sulfur, S (%) ≤: 0.015
Nickel, Ni (%): 0.35 ~ 0.65
Chromium, Cr (%): 10.00 ~ 11.00
Molybdenum, Mo (%): 0.30 ~ 0.50
Copper, Cu (%): ≤ 0.20
Vanadium, V (%): 0.14 ~ 0.20
Nitrogen, N (%): 0.04 ~ 0.08
Niobium, Nb (%): 0.05 ~ 0.11
Tungsten, W (%): 1.50 ~ 1.90
Aluminum,, Al (%): ≤ 0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Heat treatment temperature /℃| annealing: 600 ~ 770 air cooling
Heat treatment temperature /℃| Normalizing: -
Heat treatment temperature /℃| Quenching: 1100 Min.oil cooling.
Heat treatment temperature /℃| Tempering : 650 Min. air cooling..
Hardness after annealing ≤HBS: 255 Max.
Tensile strength, Rm ≥ MPa: 930
Yield strength, Rp0.2 ≥ MPa: 765
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 32.0
Impact strength, AKu ≥ J: 20
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 880mm
Square bar / Flat bar: 6mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Plate / Sheet via hot / cold rolled: T0.5 - 300mm X W60 - 1200mm X Lmm
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nuts.
Multidiameter shaft, Pressure vessel parts.
TECHNICAL SALES ASSISTANCE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry, pleased to email (sales@ccsteels.com) or call our resident team of qualified production engineers.
Hot search:
Previous page:2Cr11Mo1VNbN
Last page:IS 7806 Grade 10
Total list
Monthly rank
- 3624CrMo5
- 3342Cr4Mo2
- 3338NCD4
- 32EN 14B
- 27ASTM A739 type B11
- 27EN33 / EN 33
- 2231Ni10Cr3Mo6
- 22EN 38
- 22XC38
- 2226NiCrMoV11-5