40CrNi Stockist, 40CrNi Equivalent Steel

40CrNi
2024-09-08 12:55:29   Origin:   Remark:0 Click:

GJB 1220A Material Specification for Alloy Structure Steel Bar for Artillery Parts 40CrNi Stock Available Round bar, Flat bar, 40CrNi Forgings
 
MATERIAL DATA SHEET - GB 40CrNi

MATERIAL CATEGORY - 
Specification for Alloy Structure Steel Bar for Artillery Parts,

PRODUCT DESCRIPTION
The 
alloy is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered. 
Stock Available: Round bar diam. 20 ~ 300mm

MATERIAL SPECIFICATIONS - GJB 1220A - 2008
 
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5 ~ 900mm
Square bar / Flat bar: T6 ~ 400 X W 15 ~ 650 X Lmm
Length: Fixed length or random length or based on the customer's special requirement.
Plate & Sheet steel: T0.5 - 200mm X W10 - 1500mm X L1000 - 12000mm

TYPICAL APPLICATIONS
Alloy structural 
steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nuts.
Multidiameter shaft, Pressure vessel parts.


TYPICAL CHEMICAL COMPOSITION (mass fraction in percent - %)      
Carbon, C (%): 0.37 ~ 0.44
Silicon, Si (%): 0.17 ~ 0.37
Manganese, Mn (%): 0.50 ~ 0.80
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.020
Chromium, Cr (%): 0.45 ~ 0.75
Nickel, Ni (%): 1.00 ~ 1.40
Molybdenum, Mo (%): -
Vanadium, V (%): -
Tungsten, W (%): -
Aluminum, Al (%): -
Titanium, Ti (%): -
Ferrum, Fe (%): remainder.

MECHANICAL PROPERTIES - HEAT TREATMENT AND HARDNESS
Heat treatment temperature /℃| annealing: -.
Heat treatment temperature /℃| Normalizing:  -
Heat treatment temperature /℃| Quenching:  820 oil
Heat treatment temperature /℃| Tempering : 500 water / oil
Hardness after annealing ≤HBW:  241 Max.
Tensile strength, Rm ≥ MPa: 785
Yield strength, Rp0.2 ≥ MPa: 590
Elongation, A ≥ (%): 10.0
Reduction of area, Z ≥ (%): 50.0
Impact strength, AKu ≥ J: 55


TECHNICAL SALES ASSISTANCE & SERVICE
Customizing special 
material is welcome.
We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.

If you are interested in our products or services, or would like to learn more about us, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.

Hot search:

Previous page:8Cr3NiMoV
Last page:最后一页

Share to: