Gun steel PCr2Ni2MoV
2026-08-25 10:43:24 Origin： Remark：0 Click：
GJB 5207 Specification for alloy steel forgings of cannon barrel parts PCr2Ni2MoV round bar, plate ESR remelting process PCr2Ni2MoV hot forged, rolled, heat treated
TECHNICAL DATA SHEET - PCr2Ni2MoV
Technical standard: GJB 5207 - 2003
Usage: 57 mm barrel gun bodyStock available: round bar, hollow bar, forging block
PROFILES AND DIMENSIONS
Rod, round bar, disc (diameter): 10 ~ 500 mm
Square bar, flat bar: 10 ~ 600 mm
Forging: T20 ~ 600 X W 50 ~ 800 X L mm
TYPICAL CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): 0.32 ~ 0.42
Silicon, Si (％): 0.17 ~ 0.37
Manganese, Mn (％): 0.20 ~ 0.80
Phosphorus, P (％): ≤ 0.025
Sulfur, S (％): ≤ 0.020
Chromium, Cr (％): 1.40 ~ 1.70
Nickel, Ni (％): 1.40 ~ 1.70
Molybdenum, Mo (％): 0.35 ~ 0.50
Vanadium, V (%): 0.10 ~ 0.25
Ferrum, Fe (%): remainder.MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature / ℃ | annealing: -.
Heat treatment temperature / ℃ | normalizing:
Heat treatment temperature / ℃ | quenching: 880
Heat treatment temperature / ℃ | tempering : 510
Hardness after annealing, ≤ HB: -
Limit of proportionality: 540 / 590 Mpa
Elongation, A5 ≥ (%): 35.0Impact strength, AKv ≥ J: 17
Limit of proportionality: 635 / 685 / 735 / 785 Mpa
Elongation, A5 ≥ (%): 30.0Impact strength, AKv ≥ J: 15
Limit of proportionality: 835 / 885 / 930 Mpa
Elongation, A5 ≥ (%): 25.0Impact strength, AKv ≥ J: 15
Hardness after final heat treatment / HB: -
PRODUCT DESCRIPTION
PCr2Ni2MoV is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + quenched + tempered.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome
PRODUCT DESCRIPTION
PCr2Ni2MoV is usually produced by EAF + VD + LF / BEF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied black in the annealed condition.
Final heat treatment - normalized + quenched + tempered.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome
Raw Material Stock Available
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
Non-magnetic steel:
1.3813, X40MnCrN19
1.3816, X8MnCrN18-18
1.3817, X40MnCr18
1.3818, X55MnCrN18-4
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
Non-magnetic steel:
1.3813, X40MnCrN19
1.3816, X8MnCrN18-18
1.3817, X40MnCr18
1.3818, X55MnCrN18-4
Hot search：
Previous page：Corrosion resisting steel Nitronic 50
Last page：最后一页