14X2H3MA Alloyed Structural Steel
2026-11-03 09:11:22 Origin： Remark：0 Click：
ГОСT 4543 -1971 Chromium - Nickel - Molybdenum steel round bar 14X2H3MA heat treated forgings plate stock available ESR ingot, hot bloomed, rolled, forged, 14X2H3MA rod
TECHNICAL DATA SHEET - 14X2H3MA
Material type: 1.6Cr - 3.0Ni - 0.25Mo - 0.14C Iron-base structural steel
Technical standard: ГОСT 4543 -1971
Available on stock: round bar 35 ~ 350 mm
Material type: 1.6Cr - 3.0Ni - 0.25Mo - 0.14C Iron-base structural steel
Technical standard: ГОСT 4543 -1971
Available on stock: round bar 35 ~ 350 mm
PRODUCT DESCRIPTION
14Х2H3MA is usually produced by EAF + LF + VD / EF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
14Х2H3MA is usually produced by EAF + LF + VD / EF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment: quenched and tempered.
Rod, round bar, disc (diameter): 6.0 ~ 820 mm
Square bar, flat bar (width) : 10 ~ 550 mm
Plate, sheet via cold & hot rolled / forged: THK 0.5 ~ 320 X wide 20 ~ 800 X L mm
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
Final heat treatment: quenched and tempered.
Rod, round bar, disc (diameter): 6.0 ~ 820 mm
Square bar, flat bar (width) : 10 ~ 550 mm
Plate, sheet via cold & hot rolled / forged: THK 0.5 ~ 320 X wide 20 ~ 800 X L mm
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Steel bar and steel forgings for barrel of middle-small caliber quick firing arms.
Power generation, turbine fasteners, boiler support rods.
Process plant, fasteners, Mechanical gears, gear shaft, main axis, valve rod.
Carbon, C : 0.12 ~ 0.17
Silicon, Si : 0.17 ~ 0.37
Manganese, Mn : 0.30 ~ 0.60
Phosphorus, P : ≤ 0.025
Sulfur, S : ≤ 0.025
Chromium, Cr : 1.50 ~ 1.75
Nickel, Ni : 2.75 ~ 3.15
Molybdenum, Mo : 0.20 ~ 0.30
Ferrum, Fe : balance.
MECHANICAL PROPERTIES - HEAT TREATMENT PRACTICE
Heat treatment temperature, annealing : -
Heat working temperature : 1200 ~ 800 degree centigrade
Heat treatment temperature, quenching : 880 degree centigrade, oil quenching
Heat treatment temperature, tempering : 180 degree centigrade, water or oil cooled
Hardness under annealing condition ≤ HB : 269
Tensile strength, Rm: 932 MPa Min.
Yield strength, Rp ≥ MPa : 735 MPa Min.
Elongation, A5 : 11.0% Min.
Reduction of area, Z : 55.0% MIn.
Impact strength, AKv : 95 J Min.
Hardness after final heat treatment, HB : -
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years focus on special steel manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Further, please also check the materials in stock available:
Raw material - steels of blade for steam turbine
XM-25, S45000, GD450, C450
403 ESR, GB8732 type 12Cr12Mo, 10705BA/BB/BC
AISI 616, 422, 1.4935, X20CrMoWV12-1, 10705BU
B50A365B, 403Cb+, 1.4913, X19CrMoVNbN11-1
17-4PH, 630, 1.4542, X5CrNiCuNb16-4, 10705GU/GV/GW
M-152, S64152, 1.4938, X12CrNiMoV12-3, S151D
FV520B, S143, 1.4594, X4CrNiCuMo14-5
X22CrMoV12-1, 1.4923
13Х11Н2B2MФ, AE961W
15-5PH, XM-12, S15500
A286, AISI 660, S66286
10705MBU, 10705AJ
Non-magnetic 18.0% Manganese alloy steel:
1.3813, X40MnCrN19
1.3816, X8MnCrN18-18
1.3817, X40MnCr18
1.3818, X55MnCrN18-4
1.3813, X40MnCrN19
1.3816, X8MnCrN18-18
1.3817, X40MnCr18
1.3818, X55MnCrN18-4
Hot search：
Previous page：34CrMo Alloyed Steel, 34CrMo
Last page：446-1 Ferritic Steel
Total list
Monthly rank
- 16EN34 / EN 34
- 13EN46
- 12C15E / XC18
- 1115CrMoV5-9
- 11AISI 4330
- 1160SiMn5 /1.5142
- 11S154D
- 11SNCM420
- 11A470 Grade B Class 4
- 10815M17