2014-10-28 15:54:47 Origin: Remark:0 Click:
DIN EN 10083-2 hardened and tempered steel 35NiCr18 Round bar, Flat bar, Plate 1.5846 forgings, ESR, hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - DIN 35NiCr18
MATERIAL CATEGORY - hardened and tempered steel
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): 0.30 ~ 0.40
Silicon, Si (%): 0.15 ~ 0.35
Manganese, Mn (%): 0.40 ~ 0.80
Phosphorus, P (%)≤: 0.035
Sulfur, S (%)≤: 0.035
Chromium, Cr (%): 1.10 ~ 1.50
Molybdenum, Mo (%): -
Nickel, Ni (%): 4.25 ~ 4.75
Silicon, Si (%): 0.15 ~ 0.35
Manganese, Mn (%): 0.40 ~ 0.80
Phosphorus, P (%)≤: 0.035
Sulfur, S (%)≤: 0.035
Chromium, Cr (%): 1.10 ~ 1.50
Molybdenum, Mo (%): -
Nickel, Ni (%): 4.25 ~ 4.75
Hot working temperature /℃: 1100 ~ 850
Heat treatment temperature /℃| annealing: 580 ~ 610
Heat treatment temperature /℃| annealing: 580 ~ 610
Heat treatment temperature /℃| Normalizing: 830 ~ 860
Heat treatment temperature /℃| Quenching: 820 ~ 850 Oil or air cooling
Heat treatment temperature /℃| Tempering: 450 ~ 650
Hardness after annealing ≤HBS: -
Heat treatment temperature /℃| Quenching: 820 ~ 850 Oil or air cooling
Heat treatment temperature /℃| Tempering: 450 ~ 650
Hardness after annealing ≤HBS: -
Steel dimension /mm: 41 - 100
Tensile strength, Rm ≥ MPa: 1270 ~ 1470
Yield strength, Rp0.2 ≥ MPa: 1030
Elongation, A5 ≥ (%): 7.0
Reduction of area, Z ≥ (%): 35.0
Impact strength, AKV≥ J: 34
Tensile strength, Rm ≥ MPa: 1270 ~ 1470
Yield strength, Rp0.2 ≥ MPa: 1030
Elongation, A5 ≥ (%): 7.0
Reduction of area, Z ≥ (%): 35.0
Impact strength, AKV≥ J: 34
Round bar / Disc (diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 650mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: based on OEM.
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod.
Mechanical parts - connecting rod, bolt and nuts, Multidiameter shaft.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search:35NiCr18
Total list
Monthly rank
- 3924CrMo5
- 3738NCD4
- 36ASTM A739 type B11
- 32EN 14B
- 3142Cr4Mo2
- 29820M17 / En354
- 27EN52 & EN 52
- 27EN 38
- 2640Cr4
- 2216NC6