Description 31CrV3 Round bars, Stocklist 31CrV3 Ex-stock, Inventory 31CrV3 Plate Properties from Steelmaking, ESR melted, Blooming, Hot forging % rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATASHEET - Grade DIN 31CrV3
MATERIAL CATEGORY - Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / forgings / plate
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 650mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 300mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.28 ~ 0.35
Si (％): 0.25 ~ 0.40
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.40 ~ 0.70
Mo (％): -
V (％): 0.07 ~ 0.12
Si (％): 0.25 ~ 0.40
Mn (％): 0.40 ~ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.40 ~ 0.70
Mo (％): -
V (％): 0.07 ~ 0.12
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 220
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 830～860
Cooling medium: water / water
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 52
Hardness after tempering at temperature HRC|200℃: 50
Hardness after tempering at temperature HRC|300℃: 47
Hardness after tempering at temperature HRC|400℃: 43
Cooling medium: water / water
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 52
Hardness after tempering at temperature HRC|200℃: 50
Hardness after tempering at temperature HRC|300℃: 47
Hardness after tempering at temperature HRC|400℃: 43
INVENTORY - Forged bar
Diameter: 100mm, 80.4mm, 90mm, 125mm
Diameter: 100mm, 80.4mm, 90mm, 125mm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：31CrV3
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93