Description 80CrV2 Round bar, Plate 80CrV2 Ex-stock, Inventory 80CrV2 Shaft Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
ALLOY TOOL STEEL DATA SHEET - Grade 80CrV2
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Round bar / hollow bar / plate / forgings
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
CHEMICAL COMPOSITION (Mass weight- %)
C (％): 0.75 ~ 0.85
Si (％): 0.25 ~ 0.40
Mn (％): 0.30 ~ 0.50
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.40 ~ 0.70
Mo (％): -
V (％): 0.15 ~ 0.25
Si (％): 0.25 ~ 0.40
Mn (％): 0.30 ~ 0.50
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.40 ~ 0.70
Mo (％): -
V (％): 0.15 ~ 0.25
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050 ～ 800
Annealing temperature /℃: 680 ～ 710
Hardness after annealing ≤HBW: 250
Annealing temperature /℃: 680 ～ 710
Hardness after annealing ≤HBW: 250
Quenching temperature /℃: 800 ～ 830
Cooling medium: oil
Common tempering temperature /℃: 180~300
Hardness after tempering at temperature HRC|100℃: 63
Hardness after tempering at temperature HRC|200℃: 60
Hardness after tempering at temperature HRC|300℃: 55
Hardness after tempering at temperature HRC|400℃: 50
Cooling medium: oil
Common tempering temperature /℃: 180~300
Hardness after tempering at temperature HRC|100℃: 63
Hardness after tempering at temperature HRC|200℃: 60
Hardness after tempering at temperature HRC|300℃: 55
Hardness after tempering at temperature HRC|400℃: 50
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools.
Mechanical parts.
Air hammer tools.
Piercing tools.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 500mm
Plate / Sheet steel / Steel strip: 10mm to 1200mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：80CrV2