SKT4 /1.2713
2016-01-18 12:11:00 Origin： Remark：0 Click：
Specifications SKT4 Datasheet, JIS SKT4 Chemical, JIS SKT4 Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specification - JIS G4404/2006. We also possess the advanced precision machining equipments for catering for your different special requirements.
Technical Specification Datasheet: SKT4 & 1.2713
OFFICIAL TEST REPORT: issued by TUV - SGS - BV
MATERIAL CATEGORY: Hot work alloy tool steel
MATERIAL SPECIFICATIONS: JIS G4404 -2006
CHEMICAL COMPOSITION (WEIGHT - %)
C (％): 0.50 ~ 0.60
Si (％): 0.10 ~ 0.40
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.030
S (％)≤: 0.030
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 0.80 ~ 1.20
W (％): -
V (%): 0.05 ~ 0.15
Mo (%): 0.35 ~ 0.55
Ni (%): 1.50 ~ 1.80
HEAT TREATMENT PRACTICE AND HARDNESS
Hot working tenperature ℃ /Starting: 1050
Hot working tenperature ℃ /Starting: 1050
Hot working tenperature ℃ /Ending: 850
Annealing temperature ℃: 740~800
Hardness after annealing ≤HBW: 248
Quenching temperature ℃: 850
Cooling medium: Oil cooled
Annealing temperature ℃: 740~800
Hardness after annealing ≤HBW: 248
Quenching temperature ℃: 850
Cooling medium: Oil cooled
Tempering temperature ℃: 500
Hardness value after tempered /≥ HRC: 42
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining.
Hardness value after tempered /≥ HRC: 42
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
FEATURES AND CLASSIFICATIONS
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip: T0.20 ~ 500mm X W10 ~ 2000mm X L
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Previous page：32CrMoV3-3
Last page：55NiCrMoV7 /L6
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93