1.2064
2020-05-14 10:16:32 Origin： Remark：0 Click：
1.2064 data sheet,1.2064 Chemical, 1.2064 Specifications from Steelmaking, ESR, Blooming,Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
ALLOY TOOL STEEL - W-Nr 1.2064
PRODUCT DESCRIPTION
The alloy is usually produced by EAF VD LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
CHEMICAL COMPOSITION (WEIGHT %) - DIN 145Cr6
C (％): 0.80 ~ 0.95
Si (％): 0.15 ~ 0.45
Mn (％): 0.50 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.020
Cr (％): 1.30 ~ 1.70
Mo (％): -
V (％): -
Si (％): 0.15 ~ 0.45
Mn (％): 0.50 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.020
Cr (％): 1.30 ~ 1.70
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 750～780
Hardness after annealing ≤HBW: 225
Quenching temperature /℃: 820～850
Cooling medium: water / oil
Common tempering temperature /℃: 150～250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 60
Hardness after tempering at temperature HRC|400℃: 56
Annealing temperature /℃: 750～780
Hardness after annealing ≤HBW: 225
Quenching temperature /℃: 820～850
Cooling medium: water / oil
Common tempering temperature /℃: 150～250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 60
Hardness after tempering at temperature HRC|400℃: 56
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) or call our resident team of qualified production engineers.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 700mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1300 mm, with wall thickness ranging from 15 to 350 mm.
Hot search：1.2064
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93