1.2056 Stockist, 1.2056 Equivalent Steel
Home > Tool steel > Text

1.2056
2014-09-12 13:54:31   Origin:   Remark:0 Click:

Specifications 1.2056 datasheet, 1.2056 Chemical, 1.2056 Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL TECHNICAL STANDARD - W-Nr 1.2056

Material category - Cold work alloy tool steel 
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts  
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT 
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES  
Round bar / flat bar / square bar / plate 
Bright - peeled + polishing, centerless grinding
Forged - ring /tube  /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %) - DIN 90Cr3
C (%):     0.85 ~ 0.95
Si (%):    0.15 ~ 0.30
Mn (%):   0.20 ~ 0.40
P (%)≤:   0.030
S (%)≤:   0.030
Cr (%):    0.70 ~ 0.90
Mo (%):   —
V (%):     — 
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃:  1050~850
Annealing temperature /℃:  710~740
Hardness after annealing ≤HBW:  210
Quenching temperature /℃:  770~800
Cooling medium: water
Common tempering temperature /℃:  180~250
Hardness after tempering at temperature HRC|100℃:    65
Hardness after tempering at temperature HRC|200℃:    62
Hardness after tempering at temperature HRC|300℃:    56
Hardness after tempering at temperature HRC|400℃:    --
PROFILE & DIMENSIONS  
 
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Plate / Sheet steel / Steel strip: 1.0mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com

Hot search:1.2056