X105CrCoMo18-2
2021-03-13 09:05:45 Origin： Remark：0 Click：
Specifications X105CrCoMo18-2 Datasheet, X105CrCoMo18-2 Chemical, X105CrCoMo18-2 Property from Steelmaking (EF / VIM), ESR & VAR technique, Blooming, Hot forging / rolling, Heat treat, Straighted, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - DIN X105CrCoMo18-2
HS CODE - 72222000 / 72221100
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Alloy steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.00 ~ 1.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 16.5 ~ 18.5
Ni (％): -
Mo (%): 1.00 ~ 1.50
Co (%): 1.30 ~ 1.80
MATERIAL CATEGORY - Alloy steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.00 ~ 1.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 16.5 ~ 18.5
Ni (％): -
Mo (%): 1.00 ~ 1.50
Co (%): 1.30 ~ 1.80
V (%): 0.07 ~ 0.12
MECHANICAL PROPERTY UNDER ROOM TEMP.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: -
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW) under annealling condition: 285 Max.
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW) under annealling condition: 285 Max.
Annealing temp.: 800 ~ 850 Deg. furnace cooled.
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS AVAILABLE & DIMENSIONS
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS AVAILABLE & DIMENSIONS
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
Hot search：X105CrCoMo18-2
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93