40CrNiMoV3-3-4 is middle carbon, Chromium - Nickel - Molybdenum - Vanadium Base Tool steel, 40CrNiMoV3-3-4 Round bar, flat bar and plate available stock, Steel melting, ESR melted, Blooming, Hot forging / Hot rolling, Heat treated.
 
 

RAW MATERIAL SPECIFICATIONS - Grade 40CrNiMoV3-3-4
MATERIAL CATEGORY - cold work alloy tool 
steel 
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + VD + LF / BEF + ESR
H S CODE For Customs - 7228 4000 / 7228 6000
Official Test Certificate - issued by TUV - SGS -  BV

MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (%):  0.37 ~ 0.43
Silicon, Si (%):  1.30 ~ 1.60
Manganese, Mn (%):  0.70 ~ 0.90
Phosphorus, P (%)≤:  0.030
Sulfur, S (%)≤:  0.015
Chromium, Cr (%):  0.50 ~ 0.80
Nickel, Ni (%):  0.70 ~ 1.00
Molybdenum, Mo (%):  0.30 ~ 0.45
Vanadium, V (%):  0.07 ~ 0.12
Ferrum, Fe (%):  balance.

MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE - HARDNESS
Hot working tenperature /℃:  1050 ~ 850
Annealing temperature /℃:  650 ~ 700
Hardness after annealing ≤HBW:  255
Quenching temperature /℃:   830 ~ 870
Cooling medium:  air or oil
Common tempering temperature /℃:  160 ~ 300
Hardening value after tempering at temperature /MPa | 100℃:  HRC 56

ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special 
material is welcome.
Round bar (Diameter): 5.5 to 550mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 800 X Lmm
Heavy plate (Thickness X width): 60 ~ 400 X 80 ~ 1000 X Lmm
Length: fixed length, or based on the customer's special requirement.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:
sales@ccsteels.com.

Hot search:40CrNiMoV3-3-4

Previous page:AMS 5664
Last page:1.2741

Share to: