34CoCrMoV19-12
2023-12-24 17:39:08 Origin： Remark：0 Click：
EN ISO 4957, DIN 17350 Tool Steel Stock Available 34CoCrMoV19-12 Round bar, Flat bar, Plate and DIN 34CoCrMoV19-12 forgings ESR melted, Heat treatment.
TECHNICAL SPECIFICATION - Grade 1.2887 & 34CoCrMoV19-12
Material Category - Hot working alloy tool steel
Material Specifications - EN ISO 4957: 2000, DIN 17350
Special Melting Process: EAF + VD + LF / BEF + ESR
H S Code For Customs: 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.32 ~ 0.36
Silicon, Si (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.30 ~ 0.50
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 2.70 ~ 3.20
Molyddenum, Mo (%): 2.70 ~ 3.20
Vanadium, V (％): 0.60 ~ 0.80
Cobalt, Co (%): 4.50 ~ 5.00
Material Category - Hot working alloy tool steel
Material Specifications - EN ISO 4957: 2000, DIN 17350
Special Melting Process: EAF + VD + LF / BEF + ESR
H S Code For Customs: 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.32 ~ 0.36
Silicon, Si (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.30 ~ 0.50
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 2.70 ~ 3.20
Molyddenum, Mo (%): 2.70 ~ 3.20
Vanadium, V (％): 0.60 ~ 0.80
Cobalt, Co (%): 4.50 ~ 5.00
MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE - HARDNESS
Hot working tenperature /℃: 1050 ~ 900
Annealing temperature /℃: 720 ~ 840
Hardness after annealing ≤HBW: 320
Quenching temperature /℃: 1050 ~ 1100
Cooling medium: oil or air
Common tempering temperature /℃: 500 ~ 750
Hardening value after tempering at temperature /MPa | 500℃: HRC 55
TYPICAL APPLICATIONS
Cutting tools. Mechanical parts, Air hammer tools. Piercing tools.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar & Disc (Diameter): 5.5 to 700mm
Flat bar (Thickness X width): 10 ~ 500 X 15 ~ 600 X Lmm
Heavy plate (Thickness X width): 40 ~ 500 X 50 ~ 1000 X Lmm
Length: fixed length, random length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot working tenperature /℃: 1050 ~ 900
Annealing temperature /℃: 720 ~ 840
Hardness after annealing ≤HBW: 320
Quenching temperature /℃: 1050 ~ 1100
Cooling medium: oil or air
Common tempering temperature /℃: 500 ~ 750
Hardening value after tempering at temperature /MPa | 500℃: HRC 55
TYPICAL APPLICATIONS
Cutting tools. Mechanical parts, Air hammer tools. Piercing tools.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar & Disc (Diameter): 5.5 to 700mm
Flat bar (Thickness X width): 10 ~ 500 X 15 ~ 600 X Lmm
Heavy plate (Thickness X width): 40 ~ 500 X 50 ~ 1000 X Lmm
Length: fixed length, random length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：34CoCrMoV19-12
Total list
Monthly rank
- 35EN 28
- 1940CMD8
- 18115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 10SK85M / SK5M
- 1075Cr1
- 955NCDV7
- 9Carpenter 158