Specifications 1.2764 Datasheet, 1.2764 Chemical, 1.2764 properties steelmaking, hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing
MATERIAL DATA SHEET - W-Nr 1.2764
MATERIAL SPECIFICATIONS EN ISO 4957: 2000, DIN 17350 (1980)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.16 ~ 0.22
Si (％): 0.10 ~ 0.40
Mn (％): 0.15 ~ 0.45
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.10 ~ 1.40
Mo (％): 0.15 ~ 0.25
V (％): -
Ni (％): 3.80 ~ 4.30
Si (％): 0.10 ~ 0.40
Mn (％): 0.15 ~ 0.45
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.10 ~ 1.40
Mo (％): 0.15 ~ 0.25
V (％): -
Ni (％): 3.80 ~ 4.30
W (%): 0.30 ~ 0.50
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 620～660
Hardness after annealing ≤HBW: 255
Annealing temperature /℃: 620～660
Hardness after annealing ≤HBW: 255
Quenching temperature /℃: 780 ~ 810
Cooling medium: oil
Common tempering temperature /℃: 150~180
Hardness after tempering at temperature HRC|100℃: 62
Cooling medium: oil
Common tempering temperature /℃: 150~180
Hardness after tempering at temperature HRC|100℃: 62
Hardness after tempering at temperature HRC|200℃: 60
Hardness after tempering at temperature HRC|300℃: 58
Hardness after tempering at temperature HRC|400℃: 56
Hardness after tempering at temperature HRC|400℃: 56
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF /IFF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the
buyers' requirements.
Bars are usually supplied bright (peeling or centreless grinding) in the softened = SA condition.
Final heat treatment - heat treatment / spheroidizing annealing
MATERIAL CATEGORY: Cold work alloy tool steel
Cold work die includes cold punching mould, wire-drawing die, drawing die, coining die, thread rolling die, cold heading die, cold extrusion die, Based on the working condition, cold work die should have the high hardness, strength, abrasion resistance, toughness, hardenability, quenching degree, and other processing property. This kind of alloy tool steel belongs to high carbon alloy steel (carbon mass fraction is over 0.80%), Chromium is key element of alloy with mass fraction below 5% generally.
AVAILABLE SHAPES
Round bar / flat bar / square bar / forgings / hollow bar
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 500mm
Width: 8mm to 600mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：1.2764
Previous page：X19NiCrMo4
Last page：X45NiCrMo4
Total list
Monthly rank
- 30EN 28
- 1940CMD8
- 17115CrV3
- 15AISI M47 / ASTM M47
- 111.2333
- 11SS14 2140
- 955NCDV7
- 9SK85M / SK5M
- 8Carpenter 158
- 8SKS93