S42200 | AMS 5655 Martensitic Steel Round bar
2022-08-12 16:44:48 Origin： Remark：0 Click：
UNS S42200 is Defined as a Martensitic Stainless Steel also known as DIN 1.4935, JIS SUH616, AMS 5655, Equivalent standards are similar to one or more standards provided by the supplier. Round bar, Flat bar, Forging Available.
Typical Applications
UNS S42200 / AMS 5655 has been used typically for parts requiring corrosion resistance, stress-corrosion resistance, high strength up to 1200F ( 650℃ ), and good ductility and strength in the transverse direction in large section sizes, but usage is not limited to such applications.
Referenced Relevant Standards
ASTM A370 Mechanical Testing of Steel Products.
ASTM A604 Macroetch Testing of Consumable Electrode Remelted Steels.
ASTM E112 Determining Average Grain Size.
ASTM E353 Chemical analysis of stainless, heat-Resisting, maraging and Other Similar Chromium-Nickel-lron Steels.
Meltng Process Route
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
Chemical compositions (Mass Weight - %) - Grade UNS S42200
C (％): 0.20 ~ 0.25, Si (％): ≤ 0.50, Mn (％): 0.50 ~ 1.00, P (％)≤: 0.025, S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5, Ni (％): 0.50 ~ 1.00, Mo (％): 0.90 ~ 1.25
W (％): 0.90 ~ 1.25, V (%): 0.20 ~ 0.30, Fe (%): Balance
Cr (％): 11.0 ~ 12.5, Ni (％): 0.50 ~ 1.00, Mo (％): 0.90 ~ 1.25
W (％): 0.90 ~ 1.25, V (%): 0.20 ~ 0.30, Fe (%): Balance
Mechanical Properties under different Heat Treatment Cycle
Condition of heat treatment: Annealed
Tensile strength, TS, σb ≥/MPa: -
Yield strength, YS, σ0.2 ≥/MPa:-
Yield strength, YS, σ0.2 ≥/MPa:-
Elongation, EL, δ ≥(％): -
Reduction of area, RA, ф ≥(％): -
Hardness | HRS: ≤248
Reduction of area, RA, ф ≥(％): -
Hardness | HRS: ≤248
Condition of heat treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2h, tempered
Tensile strength, TS, σb ≥/MPa: 965
Yield strength, YS, σ0.2 ≥/MPa: 760
Yield strength, YS, σ0.2 ≥/MPa: 760
Elongation, EL, δ ≥(％): 13.0
Reduction of area, RA, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Reduction of area, RA, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2h, tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa: 585
Yield strength, σ0.2 ≥/MPa: 585
longation, δ ≥(％): 17.0
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 352
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 352
Metals, Stocklist and Services
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
With extensive Stock with a prompt delivery, Customizing special material is welcome.
Steel inquiry
Hot search：S42200 | AMS 5655 Aircraft Quality Martensitic Steel
Previous page：AMS 5629 - S13800 Aerospace Quality Steels
Last page：AMS 5630
Total list
Monthly rank
- 7MSRR 6503 - MSRR 6514 Martensitic Steel Bars
- 6GTD 450 / C450 / B50A789 Blade Steel Flat bar
- 61.4938 / X12CrNiMoV12-3 / Z12CNDV12-03 ESR Steel
- 5AMS 5643 & S17400 Martensitic Aged Steel
- 41.4935 / X20CrMoWV12-1 Round bar, Flat bar Instock
- 3AMS 5676 & N06003 & Nichrome wire rod
- 3SAE 51431 Corrosion-resistant Steel
- 31.4037 & X65Cr13 Round bar / Flat bar instock
- 3AMS 5639 & S30400 Corrosion-Resisting Steel
- 3AMS 5501 / S30400 Cold Rolled Strip, plate, sheet