X10CrNiMoV12-2-2
2020-01-18 11:00:53   Origin:   Remark:0 Click:

X10CrNiMoV12-2-2 Wholesalers Steels, X10CrNiMoV12-2-2 Ex-stock Suppliers & Manufacturers, X10CrNiMoV12-2-2 Forge bar plate machined, X10CrNiMoV12-2-2 Alloy exporter, from Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - Grade X10CrNiMoV12-2-2

MATERIAL TYPE: steel for Turbine Blade, Forged
CATAGORY: Martensitic type
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     0.08 ~ 0.13
Si (%):     0.15 ~ 0.35
Mn (%):   0.60 ~ 0.90
P (%)≤:   0.025
S (%)≤:   0.015
Cr (%):    11.4 ~ 11.5
Mo (%):   1.60 ~ 1.80
Ni (%):    2.20 ~ 2.80
V (%):     0.25 ~ 0.40
N (%):     0.020 ~ 0.040
Al (%):    ≤ 0.020
Ti (%):    ≤ 0.020
Cu (%):   ≤ 0.10
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 930
Yield strength, σ0.2/MPa: 755
Elongation, δ ≥(%): 13.0
Reduction of area, ф ≥ (%): 40.0
Hardness via heat treatment /HBW: 277 ~ 363
PRODUCT DESCRIPTION
The alloy is usually produced by EAF + AOD + LF followed by electroslag refining (ESR or VAR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 10mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 - 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.

TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (
sales@ccsteels.com) our resident team of qualified production engineers.