A182 Grade F6a
2020-01-20 09:55:54 Origin： Remark：0 Click：
Martensitic steel A182 Grade F6a Round bar, flat bar, wire rod F6a Forgings, Ex-stock Sale - Technical standards - ASTM A182 - 2018
TECHNICAL DATA SHEET - ASTM A182 Grade F6a
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: Martensitic Stainless steel
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.15
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): ≤ 1.00
Silicon, Si (％): ≤ 1.00
Silicon, Si (％): ≤ 1.00
PHosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 11.5 ~ 13.0
Molybdenum, Mo (%): -
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 11.5 ~ 13.0
Molybdenum, Mo (%): -
Nickel, Ni (%): ≤ 0.50
Niobium, Nb (%): -
Titanium, Ti (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, δ ≥(％): 18.0
Reduction of area, ф ≥ (％): 35.0
Hardness via heat treatment /HBW: 207 max.
Reduction of area, ф ≥ (％): 35.0
Hardness via heat treatment /HBW: 207 max.
HEAT TREATMENT PRACTICE
Condition: anneal
Cooling medium: furnace cool
Tempering temperature: -
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Heavy / middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Heavy / middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：X10CrNiMoV12-2-2
Last page：46MnSi4
Total list
Monthly rank
- 171.5752
- 13S15 / 5S15
- 12Austenitic steel S131
- 10S132
- 10EN33 / EN 33
- 1035CrMoA
- 1024CrMo5
- 10AMS 6499
- 920Cr1Mo1VTiB
- 928CrMoNiV4-9