X50NiCrWV13-13 ESR Ingot, 1.2731 Forgings
2023-11-29 21:17:48 Origin： Remark：0 Click：
EN ISO 4957 / DIN 17350 Material Specifications X50NiCrWV13-13 Round bar, Forgings 1.2731 ESR ingot Stock Available, Heat treatment, Cold machined.
TECHNICAL DATASHEET - DIN X50NiCrWV13-13 & W-Nr 1.2731
STOCK AVAILABLE ON HAND - ESR ingot, Round bar Diam. 20 ~ 200mm
Material Category - Hot working tool steel
Material Specifications - EN ISO 4957: 2000 , DIN 17350 (1980)
Main Chemical Elements (mass weight - %)
Carbon, C (％): 0.45 ~ 0.55
Silicon, Si (％): 1.20 ~ 1.50
Manganese, Mn (％): 0.60 ~ 0.80
Phoshorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 12.0 ~ 14.0
Molybdenum, Mo (％): -
Vanadium, V (％): 0.30 ~ 1.00
Nickel, Ni (％): 12.5 ~ 13.5
Silicon, Si (％): 1.20 ~ 1.50
Manganese, Mn (％): 0.60 ~ 0.80
Phoshorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 12.0 ~ 14.0
Molybdenum, Mo (％): -
Vanadium, V (％): 0.30 ~ 1.00
Nickel, Ni (％): 12.5 ~ 13.5
Tungsten, W (%): 1.50 ~ 2.80
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Hot working tenperature ℃: 1050～850
Annealing temperature ℃: -
Hardness after annealing ≤HBW: -
Quenching temperature ℃: 980~1030
Cooling medium: Oil
Common tempering temperature ℃: 400~600
Hot working tenperature ℃: 1050～850
Annealing temperature ℃: -
Hardness after annealing ≤HBW: -
Quenching temperature ℃: 980~1030
Cooling medium: Oil
Common tempering temperature ℃: 400~600
MELTING PROCESS
This alloy is generally smelt in electric arc furnace BEF + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
This alloy is generally smelt in electric arc furnace BEF + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：
Previous page：1.2731 Round bar & ESR Ingot Stock Available
Last page：1.3810
Total list
Monthly rank
- 6Z50MC18-4 Forgings, Bars
- 4AISI 422 SUH616 1.4935 X20CrMoWV12 Flat bar
- 4M-152 / S64152 / 1.4938 Forgings
- 4AISI 422 Flat bar / S42200 Forgings
- 417-4PH Flat bar
- 3S17400 Forged Valve Body
- 3ASTM A565 grade 616
- 3AISI 630 & 17-4PH & 1.4542 & S17400 Aging Steel
- 3S13800 bar, S13800 plate
- 3B50A365B / 403Cb+ / 1.4913 Turbine Blade Steel