1.3810 Stockist, 1.3810 Equivalent Steel

1.3810
2023-11-30 09:16:47   Origin:   Remark:0 Click:

DIN SEW 390 (1991) Material Specification Austeintic Steel 1.3810 Forgings, Flat bar, Bolts and nuts, 1.3810 Round bar, Cold worked, Heat treatment

Official Test Certificate: issued by TUV - SGSBV


RAW MATERIAL DATASHEET - Grade DIN 1.3810
Material Catetory - Non-magnetic
stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Stock Available - Round bar Diameter 55 ~ 180mm
Main Chemical Elements (mass weight - %)
Carbon, C (%):  ≤ 0.25
Silicon, Si (%):  0.50 ~ 2.00
Manganese, Mn (%):  ≤ 0.50
Phosphorus, P (%)≤:  0.060
Sulfur, S (%)≤:  0.030
Chromium, Cr (%):  24.0 ~ 26.0
Nickel, Ni (%):  -
Molybdenim, Mo (%):  -
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Soft annealing treatment temperature: 800 ~ 860 ℃
Tensile strength, σb≥ /MPa: 500 ~ 750
Yield strength, σ0.2 ≥/MPa: 285
Elongation, δ≥(%): 15.0
Impact strength, Akv ≥/J: -
PRODUCT FORMS & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 700mm
Square bar / flat bar: 10mm to 550mm
Length: fixed length, random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 - 400mm X W15 - 1000mm X L1000 - 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (
sales@ccsteels.com
) our resident team of qualified production engineers.

Hot search:1.3810

Previous page:X50NiCrWV13-13 ESR Ingot, 1.2731 Forgings
Last page:X20Cr25

Share to: