Z8CND17-04 HEAT RESISTING STEEL
2025-10-24 17:35:22 Origin： Remark：0 Click：
Z8CND17-04 is defined as a heat resisting steel & martensitic type stainless steel, to produce the high temperature components for gas turbine in the field of aviation, naval vessels
TECHNICAL DATA SHEET - Z8CND17-04
Material technical specifications - DGA - AIR 9160/C - 1973
Material category - martensitic stainless steel
Stock & inventory - diameter 16, 22, 40 ~ 120mm
Custom HS code - 7222 1100 / 7222 3000
Melting process - EF / AOD + ESR
Melting process - EF / AOD + ESR
Typical chemical elements (mass fraction %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％): ≤ 0.035
Sulfur, S (％): ≤ 0.025
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 1.50
Phosphorus, P (％): ≤ 0.035
Sulfur, S (％): ≤ 0.025
Chromium, Cr (%): 15.00 ~ 17.00
Molybdenum, Mo (%): 0.80 ~ 1.50
Nickel, Ni (%): 3.50 ~ 5.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 900 ~ 1100
Yield strength, Rp0.2 ≥ MPa: 700
Elongation, A5 ≥(％): 16.0
Reduction of area, Z ≥ (％): 45.0
Impact strength, AKv (J/cm2): 100
Annealed hardness | HB 255 Max.
Tensile strength, Rm ≥ MPa: 1100 ~ 1350
Yield strength, Rp0.2 ≥ MPa: 900
Elongation, A5 ≥ (％): 13.0
Reduction of area, Z ≥ (％): 50.0
Impact strength, AKv (J/cm2): 100
Annealed hardness | HB255 Max.
Yield strength, Rp0.2 ≥ MPa: 900
Elongation, A5 ≥ (％): 13.0
Reduction of area, Z ≥ (％): 50.0
Impact strength, AKv (J/cm2): 100
Annealed hardness | HB255 Max.
Quenching, 1020,+/-10 Deg, tempering 380 / 550, +/-5 Deg.
ADVANTAGE & STOCK GRADE
Jiangyou Longhai Special Steel Co.,Ltd, an ISO 9001-2015 Certified
Stock available - round bar, flat bar, plate, forgings
Custom 450 / XM-25, 403ESR, AISI 616 / 422 ESR, B50A365B / 403Cb+ / 1.4913
17-4PH / 630 / 1.4542, M-152 / 1.4938 / S151D, FV520B / S143 / 1.4594. X22CrMoV12-1
13Х11Н2B2MФ / AE961W, 15-5PH / XM-12 (S15500), A286 / AISI 660 / S66286
10705BU, 10705MBU, 10705AJ, 10705GU/GV/GW
Hot search：Z8CND17-04 round bar flat bar HEAT RESISTING STEEL
Previous page：10705BU CORROSION RESISTANT STEEL
Last page：最后一页
Total list
Monthly rank
- 6Marinox 17 HEAT RESISTANT STEEL
- 4X22CrMoV12-1 +QT1
- 41.4935 Heat resisting steel
- 3SAE 51430 Ferritic Stainless Steel
- 3SUH616, 1.4935, X20CrMoWV12 Turbine Blade Steels
- 3M-152 / S64152 / 1.4938 Forgings
- 3ASTM A276 Gr.44700 bright bar
- 3X19CrMoNbVN11-1 Creep-resisting steel
- 317-4PH Flat bar
- 3ASTM A565 Grade 619 HT