1.4037 & X65Cr13 Round bar / Flat bar instock
2022-11-25 17:42:15 Origin： Remark：0 Click：
1.4037 (X65Cr13) is a high carbon 13% Chromium Base Martensitic Steel, 1.4037 Round bar, Flat bar Fabricated from Steelmaking, Hot forging/rolling, Heat treated, 100% Ultrasonic flaw detection test, Cold machined.
RAW MATERIAL SPECIFICATIONS - Grade DIN 1.4037 & X65Cr13
INVENTORY on hand - Round bar diam. 60mm, Flat bar 15 X 40mm.
MATERIAL CATEGORY - 13% Chromium Base martensitic steel
MATERIAL SPECIFICATIONS - DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (mass weight %)
C (％): 0.58 ~ 0.70
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 12.5 ~ 14.5
Ni (％): -
Mo (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 12.5 ~ 14.5
Ni (％): -
Mo (％): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: annealed
Thickness/mm: -
Thickness/mm: -
Tensile strength, σb/MPa: 840 max.
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Yield strength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: -
Hardness HBS30: 265
Impact strength, Akv≥/J: -
Hardness HBS30: 265
MECHANICAL PROPERTIES ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1100 ~ 800
Heat treatment temperature and cooling methods|annealing: 730 ~ 800 air / furnace cooling
Heat treatment temperature and cooling methods|quenching: 980~1030 air or oil cooking
Heat treatment temperature and cooling methods|tempering: 100~300
Condition: Annealed or Quenched and tempered.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched + Tempered.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched + Tempered.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 350mm
Square bar / Flat bar: 10mm to 500mm
Square bar / Flat bar: 10mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W10 - 1500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W6 - 1000mm X L1000 - 2000mm
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：1.4037 X65Cr13 round bar flat bar
Previous page：S42226 & 422Cb Martensitic Steels
Last page：1.2742
Total list
Monthly rank
- 4AMS 5643 & S17400 Martensitic Aged Steel
- 3 STS 630 Condition H1150 Martensitic Ageing Steel
- 3N07718 - AMS 5662 Nickel Base Austenitic Steel
- 31.4938 / X12CrNiMoV12-3 / Z12CNDV12-03 ESR Steel
- 3S64152 & Jethete M152 Aerospace Quality Steel
- 2Free machining Steel AMS 5642 & S34720
- 2S34723 Corrosion Resisting Steel
- 2X5CrNiCuNb16-4 & 1.4542 Martensitic Stainless Steel
- 2SAE 51431 Corrosion-resistant Steel
- 2X22CrMoV12-1 | 1.4923 Creep Resisting Steel