FV520B / FV520 MARTENSITIC AGED STEEL
2026-02-05 12:50:00 Origin： Remark：0 Click：
Technical specification FV520B / FV520 martensitic stainless steel heat resistant FV520 round bar, flat bar, plate, ESR ingot in stock, precipitation hardened properties
Stock & inventory: round bar Dia.50 ~ 150 mm, ESR ingot
Material data sheet: FV520B & FV520 & 1.4594
Material specifications: DIN EN 10088 - 1
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied under annealed condition.
Heat treatment - solution treatment + aged.
The alloy is usually produced by AOD / EAF / EF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied under annealed condition.
Heat treatment - solution treatment + aged.
TYPICAL CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu (%): 1.20 ~ 2.00
Carbon, C (％): ≤ 0.07
Silicon, Si (％): ≤ 0.70
Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 13.0 ~ 15.0
Nickel, Ni (％): 5.00 ~ 6.50
Molybdenum, Mo (％): 1.20 ~ 2.00
Copper, Cu (%): 1.20 ~ 2.00
Niobium, Nb (%): 0.20 ~ 0.70
TYPICAL MECHANICAL PROPERTIES
PROFILE: round bar, Flat bar, Plate
Condition: double overaged, colution treated 1050º C +2 hours, 750-850 ºC,+2 hours 750-850 ºC
Proof stress (N/mm²): 800
Tensile strength, Rm / MPa: 925 ~ 1035
Yield strength, Rp0.2 / MPa: 775
Elongation, A5 (％): 15.0
Yield strength, Rp0.2 / MPa: 775
Elongation, A5 (％): 15.0
Hardness | HB: 277 ~ 341
Impact strength, AKv /Min: 54
TYPICAL APPLICATIONS
Typical applications include pump shafts, impellers, fasteners, fans, valves, hydraulic equipment used in oil and gas industries, petrochemical, marine and nuclear engineering, and aircraft components.
PROFILE & DIMENSIONS
Round bar / rod / disc (diameter): 6.0 to 840 mm
Square bar / flat bar: 10 to 600 mm
Plate / sheet steel / steel strip: 0.3 ~ 3 x 10 ~ 300 x L mm
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Round bar / rod / disc (diameter): 6.0 to 840 mm
Square bar / flat bar: 10 to 600 mm
Plate / sheet steel / steel strip: 0.3 ~ 3 x 10 ~ 300 x L mm
Forged steel shape: stepped shafts, and other different shapes based on OEM.
Hot search：FV520B FV520 round bar instock data sheet
Previous page：GJB 12CrNi3A
Last page：5Cr8MoVSi
Total list
Monthly rank
- 17AMS 5639 & S30400 Corrosion-Resisting Steel
- 15Turbine Blade AE961W Aerospace Martensitic Steel
- 11Free machining Steel AMS 5642 & S34720
- 10SAE 30302 / AMS 5636 Corrosion-Resistant Steel
- 9AMS 5632 & SAE 51440F High-carbon Martensitic Steel
- 9AMS 5649 - J92200 - AISI 316FM Free-machining Steels
- 8FV520B CREEP RESISTANT STEEL
- 8AMS 5678 - S17700 Aged hardening Steel Bar
- 8AMS 5631 - S44002 Martensitic Stainless Steel
- 81.2731 Round bar & ESR Ingot Stock Available