DTD 500
2017-07-13 10:49:47 Origin： Remark：0 Click：
Aerospace DTD 500 data sheet, DTD 500 Chemical, DTD 500 properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working, Peeled or rough turned machining. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION & DATASHEET - DTD 500
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TYPE OF STEEL: Ni -Cr - Mo steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.35 ~ 0.45
Si (％): ≤ 0.35
Mn (％): 0.40 ~ 0.80
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 0.50 ~ 1.00
Si (％): ≤ 0.35
Mn (％): 0.40 ~ 0.80
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 0.50 ~ 1.00
Ni (%): 2.00 ~ 3.00
Mo (％): 0.40 ~ 0.70
Mo (％): 0.40 ~ 0.70
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength σb≥/MPa: 980
Yield strength σs≥/MPa: 835
Elongation δ5≥(%): 12.0
Yield strength σs≥/MPa: 835
Elongation δ5≥(%): 12.0
Inpact strength, AKv ≥/J: -
Hardness HBS: -
Hardness HBS: -
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
Forging piece: stepped shafts with flanks / discs / tubes / slugs / donuts / cubes / other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Previous page：Z50CMNNb21-09-02Az
Last page：STS3