C10E2C
2018-01-13 20:08:18 Origin： Remark：0 Click：
Material Technical Standard BS EN - 10263-3 Cold extrusion and cold heading steel C10E2C data sheet, C10E2C Chemical composition, C10E2C Mechanical property from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test/Magnetic powder inspection, Cold working, Peeled or rough turned machining. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade C10E2C
MATERIAL CATEGORY: cold extrusion and cold heading steel
MATERIAL SPECIFICATIONS: BS EN - 10263-3 2001
MATERIAL SPECIFICATIONS: BS EN - 10263-3 2001
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.08 ~ 0.12
C (％): 0.08 ~ 0.12
Si (%): ≤ 0.30
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.025
S (％)≤: 0.025
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): -
Mo (%): -
TYPICAL MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 490 ~ 640
Yield strength, σ0.2/≥ MPa: 295
Yield strength, σ0.2/≥ MPa: 295
Elongation, δ ≥(％): 16.0
Reduction of area, (%): -
Annealed hardness, HB ≤: -
MELTING PROCESS
This alloy is generally smelt in Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
This alloy is generally smelt in Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 1.00mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
Hot search：C10E2C
Total list
Monthly rank
- 171.5752
- 13S15 / 5S15
- 12Austenitic steel S131
- 10S132
- 10EN33 / EN 33
- 1035CrMoA
- 1024CrMo5
- 10AMS 6499
- 920Cr1Mo1VTiB
- 928CrMoNiV4-9