Material Technical Standard of BS EN - 10263-4 Cold extrusion and cold heading steel 17B2 data sheet, 17B2 Chemical compositions, 17B2 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test/Magnetic powder inspection, Cold working, Peeled or rough turned machining. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade 17B2
MATERIAL CATEGORY: cold extrusion and cold heading steel
MATERIAL SPECIFICATIONS: BS EN - 10263-4 2001
MATERIAL SPECIFICATIONS: BS EN - 10263-4 2001
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.15 ~ 0.20
C (％): 0.15 ~ 0.20
Si (%): ≤ 0.30
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.025
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): -
B (%): 0.0008 ~ 0.0.005
Cu (%): ≤ 0.25
TYPICAL MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 625
Yield strength, σ0.2/≥ MPa: 505
Yield strength, σ0.2/≥ MPa: 505
Elongation, δ ≥(％): 15.0
Reduction of area, (%): 45.0
Annealed hardness, HB ≤: 237
MELTING PROCESS
This alloy is generally smelt in Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
This alloy is generally smelt in Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, EF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 1.00mm to 16mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
Hot search：17B2