Technical specifications of BS 1503 1982/9 pressure vessel alloy steel BS 629-590 data sheet, BS 629-590 Chemical composition, BS 629-590 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test & Magnetic powder inspection, Cold working, Peeled or rough turned machining. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade BS 629-590
MATERIAL CATEGORY: alloy steel bars, forge pieces for pressure vessel
MATERIAL SPECIFICATIONS: BS 1503 1982/9
MATERIAL SPECIFICATIONS: BS 1503 1982/9
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.08 ~ 0.18
C (％): 0.08 ~ 0.18
Si (%): 0.25 ~ 1.00
Mn (％): 0.30 ~ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 8.00 ~ 10.0
Ni (%): -
Mo (%): 0.90 ~ 1.10
Al (%): ≤ 0.020
TYPICAL MECHANICAL PROPERTY
Tensile strength,σb/≥ MPa: 415
Yield strength, σ0.2/≥ MPa: 205
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 30.0
Reduction of area, (%): -
Annealed hardness, HB ≤: 179
MELTING PROCESS
This alloy is generally air melted of Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, or + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of VIM + Vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 450mm
Square bar / Flat bar: THK1.0 to 200mm X Width 3 ~ 450mm
This alloy is generally air melted of Non-VIM + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, or + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of VIM + Vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.50mm to 450mm
Square bar / Flat bar: THK1.0 to 200mm X Width 3 ~ 450mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. E-mail: lh.steel@hotmail.com