Material Specification ASTM A182 Grade F5 Round bar, Inventory A182 Gr. F5 Plate, A182 Grade F5 Sheet, P5 Hot forging, Hot rolling, Heat treatment.
TECHNICAL DATA SHEET - ASTM A182 Grade F5
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 5Cr- 0.5Mo Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.44 ~ 0.65
Nickel, Ni (%): -
Niobium, Nb (%): -
Titanium, Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, A5 ≥(％): 20.0
Reduction of area, Z ≥ (％): 30.0
Hardness via heat treatment /HBW: 143 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Disc (diameter): 5.5mm to 950mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W200- 1200mm X L1000-5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 5Cr- 0.5Mo Alloy steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.15
Manganese, Mn (％): 0.30 ~ 0.60
Silicon, Si (％): ≤ 0.50
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (%): 4.00 ~ 6.00
Molybdenum, Mo (%): 0.44 ~ 0.65
Nickel, Ni (%): -
Niobium, Nb (%): -
Titanium, Ti (%): -
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 485
Yield strength, σ0.2/MPa: 275
Elongation, A5 ≥(％): 20.0
Reduction of area, Z ≥ (％): 30.0
Hardness via heat treatment /HBW: 143 ~ 217
HEAT TREATMENT PRACTICE
Condition: annealed 955 Deg.
Cooling medium: furnace cool
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Disc (diameter): 5.5mm to 950mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 400mm X W200- 1200mm X L1000-5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：
Total list
Monthly rank
- 21AISI/SAE 6135
- 1852CrMoV4
- 17X46Cr13
- 1638NiCrMo4
- 16ASTM A182 type F11 Class 1
- 14805A22
- 14AMS 6320
- 141.0460
- 1425MNDC6
- 1426NiCrMoV14-5