1.8151
2020-07-24 08:57:06 Origin： Remark：0 Click：
Description 1.8151 datasheet, 1.8151 Chemical, 1.8151 Properties Steelmaking, ESR & VAR technique, Blooming, Hot forging & rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL SPECIFICATION DATASHEET - DIN 1.8151
MATERIAL CATEGORY: Hot rolled Spring steel
MATERIAL SPECIFICATIONS: DIN EN 10089
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.40 ~ 0.50
Si (％): 1.30 ~ 1.70
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.025
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): 0.40 ~ 0.80
Mo (%): -
V (％): 0.07 ~ 0.25
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Delivery hardness: HBW 248 max.
Tensile strength, ≥|σb/MPa: -
Yield strength, ≥|σs/MPa: -
Elongation, ≥| δ5(%): -
Reduction of area, ≥ |ψ(%): -
Impact strength, ≥|AKV - DVM-V /J: -
Yield strength, ≥|σs/MPa: -
Elongation, ≥| δ5(%): -
Reduction of area, ≥ |ψ(%): -
Impact strength, ≥|AKV - DVM-V /J: -
PRODUCT DESCRIPTION
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
The alloy is usually produced by EAF / BEF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment
AVAILABLE PRODUCT PROFILE
Round bar / Wire rod (Diameter1): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter1): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1200mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD30 - 1200mm, with wall thickness ranging from 15 to 350 mm.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：1.8151