TECHNICAL SPECIFICATION - BS970 Part 3
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
C (％): 0.40 ~ 0.45
Mn (％): 0.50 ~ 0.80
Si (％): 0.10 ~ 0.35
P (％)≤: 0.035
S (％)≤: 0.015
Cr (%): 0.90 ~ 1.50
Ni (%): -
Mo (%): 0.20 ~ 0.35
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: 850, oil
Tempering temperature /℃: 560, water or oil
Tensile strength,σb/≥ MPa: 1030
Yield strength, σ0.2/≥ MPa: 930
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥(％): 40.0
Hardness in annealed condition: HB 217 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.