22Mo4 Steels Ex-stock, Alloy 22Mo4 Suppliers, Properties 22Mo4 Forging Bar Plate, Grade 22Mo4 Technical specifications Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
MATERIAL DATA SHEET - DIN 22Mo4
MATERIAL CATEGORY: High temperature structural steel
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS
DIN EN 10028-2 (2003), DIN 17755 (1983)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.18 ~ 0.25
Si (％): 0.20 ~ 0.40
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): ≤ 0.30
Mo (％): 0.30 ~ 0.40
Ni (％): —
Si (％): 0.20 ~ 0.40
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): ≤ 0.30
Mo (％): 0.30 ~ 0.40
Ni (％): —
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1100～850
Heat treatment temperature /℃|annealing / normalizing : 660～700
Heat treatment temperature /℃|quenching: 880~920 oil
Heat treatment temperature /℃|tempering: 600~660
HBS: 145~175
(≥)| σb/MPa: 490～590
(≥)| σs/MPa: 295
(≥)| δ5(%): 20
(≥)| AKV/J: 55
Heat treatment temperature /℃|annealing / normalizing : 660～700
Heat treatment temperature /℃|quenching: 880~920 oil
Heat treatment temperature /℃|tempering: 600~660
HBS: 145~175
(≥)| σb/MPa: 490～590
(≥)| σs/MPa: 295
(≥)| δ5(%): 20
(≥)| AKV/J: 55
MECHANICAL PROPERTY UNDER HIGH TEMPERATURE
Yield strength σ0.2≥/MPa|200℃: -
Yield strength σ0.2≥/MPa|300℃: 275
Yield strength σ0.2≥/MPa|350℃: 255
Yield strength σ0.2≥/MPa|400℃: 235
Yield strength σ0.2≥/MPa|450℃: 206
Yield strength σ0.2≥/MPa|500℃: 186
Yield strength σ0.2≥/MPa|300℃: 275
Yield strength σ0.2≥/MPa|350℃: 255
Yield strength σ0.2≥/MPa|400℃: 235
Yield strength σ0.2≥/MPa|450℃: 206
Yield strength σ0.2≥/MPa|500℃: 186
AVAILABLE SHAPES
Black bar /Flat bar / Square bar /Pipe, /Steel strip, /sheet
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
Mechanical gears, gear shaft, main axis, valve rod
Mechanical parts - connecting rod, bolt and nut
Multidiameter shaft
Pressure vessel, seamless pipe
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. Email: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.