1.6772 datasheet,1.6772 chemical,1.6772 heat treatment

1.6772
2021-07-30 10:31:13   Origin:   Remark:0 Click:

Specifications 1.6772 Datasheet, Stocklist 1.6772 Chemical, Inventory 1.6772 Suppliers Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL DAASHEET - Grade 1.6772

Official Test Certificate: issued by TUV - SGS -  BV
MATERIAL TYPE - Quenched and tempered steel
MATERIAL STANDARDS - DIN EN 10084
CHEMICAL COMPOSITION ( Mass Weight % )
C (%):     0.18 ~ 0.25
Si (%):     0.15 ~ 0.40
Mn (%):   0.30 ~ 0.50
P (%)≤:   0.020
S (%)≤:   0.010
Cr (%):    1.20 ~ 1.50
Ni (%):    3.40 ~ 4.00
Mo (%):   0.25 ~ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength σb≥/MPa:  985
Yield strength σs≥/MPa: 815
Elongation δ5 ≥(%): 20.0
Reduction of area  ψ(%) ≥:   -
TYPICAL APPLICATIONS
Alloy structural steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Power generation – turbine fasteners – boiler support rods
Process plant – fasteners
Mechanical gears, gear shaft, main axis, valve rods
Mechanical parts - connecting rod, bolt and nut
Multidiameter shafts
AVAILBALE FROMS & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T20 - 300mm X W60 - 1000mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: