Steel EN 363 Round bar, Flat bar, plate and forgings Steelmaking, Hot forging/rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined.
TECHNICAL DATA SHEET - Grade EN 363
MATERIAL CATEGORY - alloy steel 0.65Cr-0.55Ni-0.10Mo series
TECHNICAL SPECIFICATION - BS970 Part 7
MELTING PROCESS - Consumable electrode remelted steel
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
OFFICIAL TEST REPORT - issued by TUV - SGS -  BV
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (%):  0.22 ~ 0.26
Manganese, Mn (%):  0.70 ~ 1.00
Silicon, Si (%):  0.10 ~ 0.35
Phosphorus, P (%)≤:  0.030
Sulfur, S (%)≤:  0.015
Chromium, Cr (%):  0.55 ~ 0.80
Nickel, Ni (%):  0.40 ~ 0.70
Molybdenum, Mo (%):  0.08 ~ 0.15
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:  -
Tempering temperature /℃:  -
Tensile strength,σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 815
Elongation, δ ≥(%):  12.0
Reduction of area, ф ≥(%):  -
Hardness in condition of annealing +A: HB 269
MELTING PROCESS & APPLICATION
This 
alloy is generally smelt in Electric Arc Furnace  (EAF) + LF + VD, EF + Electroslag remelting (ESR). 
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. 
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 450mm
Square bar / Flat bar: 10mm to 610mm
Rolled / forged plate: 10mm to 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.

Hot search:EN 363

Previous page:1.2607
Last page:AMS 6260

Share to: