31Ni10Cr3Mo6 Stockist, 31Ni10Cr3Mo6 Equivalent Steel

31Ni10Cr3Mo6
2023-10-16 08:42:43   Origin:   Remark:0 Click:

IS 1570 - 4 Material Specification Cr-Ni-Mo Alloy Steel 31Ni10Cr3Mo6 Round bar, Flat bar, Forgings, 31Ni10Cr3Mo6 Heat treatment, Cold machined.
TECHNICAL SPECIFICATION DATASHEET - Grade 31Ni10Cr3Mo6
Material Category - 0.5Cr-1.8Ni-0.25Mo Base Structural
Alloy Steel
Material Specifications - IS 1570 - 4 (1988 / 2018 ) 
Special Melting Process - EAF + VD + LF / BEF + ESR
H S CODE For Customs: 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS -  BV

MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%):  0.27 ~ 0.35
Silicon, Si (%):  0.10 ~ 0.35
Manganese, Mn (%):  0.40 ~ 0.70
Phosphorus, P (%) ≤:  0.035
Sulfur, S (%) ≤:  0.025
Chromium, Cr (%):  0.50 ~ 0.80
Nickel, Ni (%):  2.25 ~ 2.75
Molybdenum, Mo (%):  0.40 ~ 0.70
Ferrum, Fe (%):  Balance.

MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE
Hot working tenperature /℃:  1100 ~ 850
Annealing temperature /℃:  650 ~ 700
Quenching temperature /℃:  860
Cooling medium:  oil or water
Common tempering temperature /℃: -
Forms: Round bar, flat bar, plate, shaft
Tensile strength, σb/≥ MPa:  1080
Yield strength, σ0.2/MPa:  815
Elongation, δ ≥(%):  8.0
Reduction of area, ф ≥ (%):  -
Hardness via annealed /HBW:  269 max.
 
SUPERIOR SERVICE & PRODUCT PROFILE 
Third party inspection service.
Export packing / Export documents.
CNC saw cutting.
Marking by stamping or printing.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Round bar & Disc (diameter): 5.5 to 800mm
Flat bar (thickness X width): 10 ~ 350 * 20 ~ 610 * Lmm
Heavy plate (thickness X width): 20 ~ 500 * 30 ~ 1200 * Lmm
Length: fixed length, random length or based on the customer's special requirement.

TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.

Hot search:31Ni10Cr3Mo6

Previous page:Magnadur 509
Last page:T40W8Cr5V2

Share to: