Quenched and tempered Alloy Steel 1.6962 high temperature alloy steel is used for larger preshaped components in turbine and generator installations, shafts and discs
MATERIAL TECHNICAL DATASHEET - 1.6962
Material Category: Hardened and tempered steel
Material Specification - SEW 555 or by agreement
Melting process way - EF + Consumable electrode remelted
HS code for Customs: 7228 4000 / 7228 5000 / 7228 6000
Main Chemical composition (mass weight - %)
Carbon, C (%): 0.22 ~ 0.28
Silicon, Si (%): ≤ 0.15
Manganese, Mn (%): 0.15 ~ 0.40
Phosphorus, P (%) ≤: 0.020
Sulfur, S (%) ≤: 0.010
Chromium, Cr (%): 1.50 ~ 2.00
Molybdenum, Mo (%): 0.40 ~ 0.60
Nickel, Ni (%): 2.80 ~ 3.20
Vanadium, V (%): 0.05 ~ 0.15
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 277
Tensile strength, Rm ≥ MPa: 850 ~ 1000
Yield strength, Rp0.2 ≥ MPa: 700
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
Hot working temperature /℃: 1050 ~ 850
Hardness after annealing ≤HBS: 277
Tensile strength, Rm ≥ MPa: 850 ~ 1000
Yield strength, Rp0.2 ≥ MPa: 700
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 40.0
PRODUCT DESCRIPTION
Alloy structural steel is provided with higher yield strength, tensile strength, endurance strength, yield ratio (about 0.85 generally ) enough plasticity and toughness.
The concentration of alloy element of this kind of steel is quite high, mainly are corrosion resistant steel, heat resistant steel, wear resistant steel, and other special steels of physical and chemical properties. Alloy structural steel has preferable mechanical property than that of carbon structural steel, high performance of heat treatment especially.
The alloy is usually produced by EAF / VD / LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
FORMS & DIMENSIONS AVAILABLE
Round bar / Disc (diameter): 5.5mm to 700mm
Square bar / Flat bar: 8mm to 550mm
Steel sheet: thickness 1.0 ~ 4.0mm, width 10 ~ 1000mm X length 1000/2000mm - Standard size
Length: random length or based on the customer's special requirement
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search:
Previous page:2Cr12NiMo1W1V
Last page:SNB21-5
Total list
Monthly rank
- 3624CrMo5
- 3338NCD4
- 33EN 14B
- 3342Cr4Mo2
- 28EN33 / EN 33
- 27ASTM A739 type B11
- 22EN 38
- 22XC38
- 2231Ni10Cr3Mo6
- 2226NiCrMoV11-5