GJB 1951-94 Material Specification for Quality Structure Steel Bar for Aviation 16Cr2MnTiA Stock Available Round bar, Flat bar 16Cr2MnTiA Forgings
 
MATERIAL STANDARD DATASHEET - GJB 16Cr2MnTiA

MATERIAL CATEGORY - Sp
ecification for Quality Structure Steel Bars for Aviation.

PRODUCT DESCRIPTION
The 
alloy is usually produced by EAF + VD + LF / BEF / VIM followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered. 
Stock Available: Round bar diam. 10 ~ 380mm
 
PRODUCT PROFILE & DIMENSIONS
Round bar & Disc (diameter): 5.5mm to 850mm
Square bar / Flat bar: 6mm to 600mm
Length: Fixed length or random length or based on the customer's special requirements.
Plate & Sheet steel: T2.0 ~ 350mm X W10 ~ 1500mm X Lmm


TYPICAL APPLICATIONS
Alloy structural 
steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Mechanical parts - connecting rod, bolt and nuts.
Multidiameter shaft, Pressure vessel parts.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod

MATERIAL SPECIFICATIONS - GJB 1951 - 94

MAIN CHEMICAL COMPOSITION (mass weight - %)      
Carbon, C (%): 0.13 ~ 0.18
Manganese, Mn (%): 1.00 ~ 1.30
Silicon, Si (%): 0.17 ~ 0.37
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%): 1.50 ~ 1.80
Nickel, Ni (%): ≤ 0.50
Molybdenum, Mo (%): -
Vanadium, V (%): -
Tungsten, W (%): -
Titanium, Ti (%): 0.06 ~ 0.12.

MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature /℃| annealing: -.
Heat treatment temperature /℃| Normalizing:  -
Heat treatment temperature /℃| Quenching:  790 ~ 860 oil
Heat treatment temperature /℃| Tempering : 160 ~ 180 air
Hardness after annealing, ≤ HBW:  156 ~ 269
Tensile strength, Rm ≥ MPa: 1030
Yield strength, Rp0.2 ≥ MPa: 785
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 55.0
Impact strength, AKu ≥ J: 85
Hardness after final heat treatment / HBW:  311 ~ 363
 
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special 
material is welcome.

We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.

If you meet further on any technical enquiry, pleased to email ( sales@ccsteels.com.) or call our resident team of qualified production engineers.

Hot search:

Previous page:13Ni14Cr3
Last page:最后一页

Share to: