30Cr2Ni2WA Stockist, 30Cr2Ni2WA Equivalent Steel

30Cr2Ni2WA
2024-10-18 10:43:00   Origin:   Remark:0 Click:

GJB 1951-94 Material Specification for Quality Structure Steel Bars for Aviation 30Cr2Ni2WA Round bar, Flat bar 30Cr2Ni2WA Forgings Processing
 
TECHNICAL DATA SHEET - GJB 30Cr2Ni2WA

MATERIAL CATEGORY - Sp
ecification for Quality Structure Steel Bars for Aviation.
 
TYPICAL APPLICATIONS
Alloy structural 
steels are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on. 
Mechanical parts - connecting rod, bolt and nuts.
Multidiameter shaft, Pressure vessel parts.
Power generation – turbine fasteners – boiler support rods.
Process plant – fasteners, Mechanical gears, gear shaft, main axis, valve rod.

PRODUCT DESCRIPTION
The 
alloy is usually produced by EAF + VD + LF / BEF / VIM followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered. 

 
PRODUCT PROFILE & DIMENSIONS
Round bar & rod & disc (diameter): 5.5 ~ 920mm
Square bar & flat bar: 8 ~ 650mm
Plate & Sheet: cold & hot rolled / forged T 2.0 ~ 350 X W 10 ~ 1200 X L mm
 
MATERIAL SPECIFICATIONS - GJB 1951 - 94

CHEMICAL COMPOSITIONS (mass fraction - %)      
Carbon, C (%): 0.27 ~ 0.34
Manganese, Mn (%): 0.30 ~ 0.60
Silicon, Si (%): 0.17 ~ 0.37
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.015
Chromium, Cr (%):  1.60 ~ 2.00
Nickel, Ni (%): 1.40 ~ 1.80
Vanadium, V (%): -
Molybdenum, Mo (%): -
Tungsten, W (%): 1.20 ~ 1.60
Ferrum, Fe (%): balance.

MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Heat treatment temperature /℃| annealing: -.
Heat treatment temperature /℃| Normalizing:  -
Heat treatment temperature /℃| Quenching:  850 ~ 870 oil cooling
Heat treatment temperature /℃| Tempering : 540 ~ 620 air cooling
Hardness after annealing, ≤ HBW:  255.
Tensile strength, Rm ≥ MPa: 980
Yield strength, Rp0.2 ≥ MPa: 835
Elongation, A5 ≥ (%): 12.0
Reduction of area, Z ≥ (%): 55.0
Impact strength, AKu ≥ J: 94
Hardness after final heat treatment / HBW:  302 ~ 341.
 
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special 
material is welcome.

We closely cooperate with the professional inspection partners to strictly control the quality and improve the quality manage system, and guarantee the goods delivery each time. It is proved that we are worth of trusting and will be the strategic partner of the supplying chains in the special steels field.

If you are interested in our products or services, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.

Hot search:

Previous page:AM 350
Last page:最后一页

Share to: